Surface-treated galvanized steel sheet with superior flat-portion corrosion resistance, blackening resistance, and appearance and corrosion resistance after press forming and aqueous surface-treatment liquid for galvanized steel sheet
An aqueous surface-treatment liquid is a treatment liquid containing a water-soluble zirconium compound, water-dispersive particulate silica, a silane coupling agent, a vanadic acid compound, a phosphoric acid compound, a nickel compound, and an acrylic resin emulsion in particular proportions. A surface-treated galvanized steel sheet produced using the treatment liquid is a galvanized steel sheet having a surface-treatment coating on a surface thereof, and the coating contains a zirconium compound, particulate silica, a silane-coupling-agent-derived component, a vanadic acid compound, a phosphoric acid compound, a nickel compound, and an acrylic resin in particular proportions. The amount of coating on a zirconium basis is 10 to 200 mg/m 2 . This surface-treated galvanized steel sheet is chromate-free and has superior flat-portion corrosion resistance, blackening resistance, and appearance and corrosion resistance after press forming.
1. An aqueous surface-treatment liquid for a galvanized steel sheet having superior flat-portion corrosion resistance, blackening resistance, and appearance and corrosion resistance after press forming, comprising a water-soluble zirconium compound (A) selected from the group consisting of sodium zirconium carbonate and ammonium zirconium carbonate; water-dispersive particulate silica (B); a silane coupling agent (C) selected from the group consisting of γ-aminopropyltriethoxysilane, γ-glycidoxypropyltrimethoxysilane and γ-aminopropyltrimethoxysilane; a vanadic acid compound (D) selected from the group consisting of sodium vanadate and ammonium vanadate; a phosphoric acid compound (E) selected from the group consisting of phosphoric acid, ammonium phosphate and diphosphonic acid; a nickel compound (F) selected from the group consisting of nickel nitrate hexahydrate and nickel sulfate hexahydrate; and an acrylic resin emulsion (G) selected from the group consisting of styrene-ethylmethyacrylate-n-butylacrylate-acrylic acid and methylmethacrylate-2-ethylhexylacrylate-acrylic acid, so as to satisfy the following conditions (1) to (7):
(1) the mass ratio (B)/(A) of the amount of water-dispersive particulate silica (B) to the amount of water-soluble zirconium compound (A) on a zirconium basis=0.1 to 1.2;
(2) the mass ratio (C)/(A) of the amount of silane coupling agent (C) to the amount of water-soluble zirconium compound (A) on a zirconium basis=0.5 to 3.0;
(3) the mass ratio (D)/(A) of the amount of vanadic acid compound (D) on a vanadium basis to the amount of water-soluble zirconium compound (A) on a zirconium basis=0.02 to 0.15;
(4) the mass ratio (E)/(A) of the amount of phosphoric acid compound (E) on a phosphorus basis to the amount of water-soluble zirconium compound (A) on a zirconium basis=0.03 to 0.30;
(5) the mass ratio (F)/(A) of the amount of nickel compound (F) on a nickel basis to the amount of the water-soluble zirconium compound (A) on a zirconium basis=0.005 to 0.10;
(6) the mass ratio (SI)/(A) of the total amount (SI) of water-dispersive particulate silica (B) and silane coupling agent (C) on a silicon basis to the amount of water-soluble zirconium compound (A) on a zirconium basis=0.15 to 1.0; and
(7) the mass ratio (G)/(X) of the solid content of the acrylic resin emulsion (G) to the total solid content (X) of the aqueous surface-treatment liquid=0.005 to 0.18.
2. The aqueous surface-treatment liquid for a galvanized steel sheet according to claim 1 , further comprising a wax (H) so as to satisfy the following condition (8):
(8) the mass ratio (H)/(X) of the solid content of the wax (H) to the total solid content (X) of the aqueous surface-treatment liquid=0.01 to 0.10.
3. A method for producing a surface-treated galvanized steel sheet having superior flat-portion corrosion resistance, blackening resistance, and appearance and corrosion resistance after press forming, the method comprising applying the aqueous surface-treatment liquid according to claim 1 to a surface of a galvanized steel sheet so that the amount of coating on a zirconium basis is 10 to 200 mg/m 2 and drying the coating.
4. A surface-treated galvanized steel sheet having superior flat-portion corrosion resistance, blackening resistance, and appearance and corrosion resistance after press forming, comprising a galvanized steel sheet having a surface-treatment coating on a surface thereof, the coating containing a zirconium compound (a) selected from the group consisting of sodium zirconium carbonate and ammonium zirconium carbonate; particulate silica (b); a silane coupling-agent-derived component (c) selected from the group consisting of γ-aminopropyltriethoxysilane, γ-glycidoxypropyltrimethoxysilane and γ-aminopropyltrimethoxysilane; a vanadic acid compound (d) selected from the group consisting of sodium vanadate and ammonium vanadate; a phosphoric acid compound (e) selected from the group consisting of phosphoric acid, ammonium phosphate and diphosphonic acid; a nickel compound (f) selected from the group consisting of nickel nitrate hexahydrate and nickel sulfate hexahydrate; and an acrylic resin (g) selected from the group consisting of styrene-ethylmethyacrylate-n-butylacrylate-acrylic acid and methylmethacrylate-2-ethylhexylacrylate-acrylic acid, so as to satisfy the following conditions (1) to (7):
(1) the mass ratio (b)/(a) of the amount of particulate silica (b) to the amount of zirconium compound (a) on a zirconium basis=0.1 to 1.2;
(2) the mass ratio (Si)/(a) of the total amount (Si) of particulate silica (b) and silane-coupling-agent-derived component (c) on a silicon basis to the amount of zirconium compound (a) on a zirconium basis=0.15 to 1.0;
(3) the mass ratio (d)/(a) of the amount of vanadic acid compound (d) on a vanadium basis to the amount of zirconium compound (a) on a zirconium basis=0.02 to 0.15;
(4) the mass ratio (e)/(a) of the amount of phosphoric acid compound (e) on a phosphorus basis to the amount of zirconium compound (a) on a zirconium basis=0.03 to 0.30;
(5) the mass ratio (f)/(a) of the amount of nickel compound (f) on a nickel basis to the amount of zirconium compound (a) on a zirconium basis=0.005 to 0.10;
(6) the mass ratio (g)/(x) of the amount of acrylic resin (g) to the total solid content (x) of the coating=0.005 to 0.18; and
(7) the mass ratio (c)/(a) of the amount of the silane-coupling-agent-derived component (c) to the amount of zirconium compound (a) on a zirconium basis=0.5 to 3.0;
wherein the amount of coating on a zirconium basis is 10 to 200 mg/m 2 .
5. The surface-treated galvanized steel sheet having superior flat-portion corrosion resistance, blackening resistance, and appearance and corrosion resistance after press forming according to claim 4 , wherein the surface-treatment coating further contains a wax (h) so as to satisfy the following condition (7):
(7) the mass ratio (h)/(x) of the amount of wax (h) to the total solid content (x) of the coating=0.01 to 0.10.
6. A method for producing a surface-treated galvanized steel sheet having superior flat-portion corrosion resistance, blackening resistance, and appearance and corrosion resistance after press forming, the method comprising applying the aqueous surface-treatment liquid according to claim 2 to a surface of a galvanized steel sheet so that the amount of coating on a zirconium basis is 10 to 200 mg/m 2 and drying the coating.