Method for filling with electrode active material and method for producing all-solid-state cell
View Patent ↗A solid electrolyte structure containing a porous solid electrolyte is prepared. At least the porous solid electrolyte of the solid electrolyte structure is immersed in a first sol solution containing at least a precursor of an electrode active material as a solute. Then, the first sol solution, in which the porous solid electrolyte is immersed, is heated. A solvent of the first sol solution is evaporated by the heating, whereby a pore of the porous solid electrolyte is filled with a high concentration (a large amount) of the electrode active material precursor.
1. A method for filling a pore of a porous solid electrolyte with an electrode active material, comprising:
an immersion step of immersing the porous solid electrolyte in a precursor solution containing at least a precursor of the electrode active material as a solute; and
a heating step of heating the precursor solution in which the porous solid electrolyte is immersed.
2. A method according to claim 1 , further comprising a thermal treatment step of, after the heating step, subjecting the precursor of the electrode active material filling the pore of the porous solid electrolyte to a thermal treatment, thereby converting the precursor of the electrode active material to the electrode active material.
3. A method according to claim 1 , further comprising a pretreatment step of, before the immersion step, immersing the porous solid electrolyte in a pretreatment solution containing at least a surfactant as a solute.
4. A method according to claim 3 , wherein the pretreatment solution and the precursor solution contain the same solvent.
5. A method according to claim 1 , wherein in the immersion step, after being vacuum-deaerated, the porous solid electrolyte is immersed in the precursor solution.
6. A method according to claim 1 , wherein the porous solid electrolyte comprises an oxide or a phosphate compound.
7. A method according to claim 1 , wherein the porous solid electrolyte comprises an LLT (Li 3x La 2/3−x TiO 3 , 0≦x≦2/3), an LAMP (Li 1+x Al x M 2−x (PO 4 ) 3 , 0≦x≦1, M is a tetravalent transition metal such as Ge, Ti or Zr), or an aluminum (Al)-containing ceramic material having a garnet-type or garnet-like-type crystal structure containing lithium (Li), lanthanum (La), zirconium (Zr), and oxygen (O).
8. A method according to claim 1 , wherein the electrode active material comprises an oxide or a phosphate compound.
9. A method according to claim 1 , wherein the electrode active material comprises a lithium-manganese composite oxide, a lithium-cobalt composite oxide, or an LVP (Li m V 2 (PO 4 ) 3 , 1≦m≦5).
10. A method for filling a pore of a porous solid electrolyte with an electrode active material, comprising
an immersion step of immersing the porous solid electrolyte in an electrode active material solution containing at least a fine particle of the electrode active material as a solute, and
a heating step of heating the electrode active material solution in which the porous solid electrolyte is immersed.
11. A method for producing an all-solid-state cell, comprising at least an electrode active material filling process of filling a pore of a porous solid electrolyte with an electrode active material, wherein
the electrode active material filling process comprises:
an immersion step of immersing the porous solid electrolyte in a precursor solution containing at least a precursor of the electrode active material as a solute; and
a heating step of heating the precursor solution in which the porous solid electrolyte is immersed.
12. A method according to claim 11 , further comprising a thermal treatment step of, after the heating step, subjecting the precursor of the electrode active material filling the pore of the porous solid electrolyte to a thermal treatment, thereby converting the precursor of the electrode active material to the electrode active material.
13. A method for producing an all-solid-state cell, comprising at least an electrode active material filling process of filling a pore of a porous solid electrolyte with an electrode active material, wherein
the electrode active material filling process comprises:
an immersion step of immersing the porous solid electrolyte in an electrode active material solution containing at least a fine particle of the electrode active material as a solute; and
a heating step of heating the electrode active material solution in which the porous solid electrolyte is immersed.