Coated steel sheet
View Patent ↗A coated steel sheet coated with a composite coat, wherein said composite coat is a coat formed by compounding ethylene-unsaturated carboxylic acid copolymerization resin particles (A) having an average particle diameter of 20 to 100 nm and a silanol group and/or an alkoxysilyl group, silicon oxide particles (B) having an average particle diameter of 5 to 50 nm and an organic titanium compound (C), and wherein an amount of a coat of said composite coat is 0.5 to 3 g/m 2 .
1. A coated steel sheet coated with a composite coat,
wherein said composite coat is a coat formed by compounding
ethylene-unsaturated carboxylic acid copolymerization resin particles (A) having an average particle diameter of 20 to 100 nm and a silanol group and/or an alkoxysilyl group, which is obtained by reacting a water dispersion of ethylene-unsaturated carboxylic acid copolymerization resin particles with an epoxy group-containing silane compound,
silicon oxide particles (B) having an average particle diameter of 5 to 50 nm,
an organic titanium compound (C),
a phosphate compound, and
at least one compound (D) selected from the group consisting of a thiocarbonyl compound, a niobium oxide and a guanidine compound,
wherein an amount of a coat of said composite coat is 0.5 to 3 g/m 2 .
2. The coated steel sheet according to claim 1 ,
wherein in the composite coat, an amount of the silicon oxide particle (B) is 5 to 100% by mass with respect to that of the resin particle (A) and the content of a titanium atom is 0.05 to 3% by mass with respect to the total amount of a coat.
3. The coated steel sheet according to claim 1 ,
wherein the resin particle (A) comprises an ethylene-methacrylic acid copolymerization resin.
4. The coated steel sheet according to claim 2 ,
wherein the resin particle (A) comprises an ethylene-methacrylic acid copolymerization resin.