Laser welding method for steel sheet
The present invention provides a laser welding method for steel sheets. The laser welding method includes irradiating a low heat input laser beam to a weld zone with a uniform welding pattern of a zigzag shape, with a constant pitch, and with a constant welding speed, so that autogenous welding may be achieved without a feed wire, such that cost of material may be reduced and joinability and performance may be improved.
1. A method for laser welding, the method comprising:
providing an underlying metal sheet;
providing an overlying metal sheet that is positioned over a portion of the underlying metal sheet; and
irradiating a weld zone with a low heat input laser beam,
wherein:
the weld zone includes a selected edge of the overlying metal sheet and an upper surface region of the underlying metal sheet that is adjacent to the selected edge;
the laser beam is moved across the weld zone in a zigzag pattern;
the laser beam is oscillated by an Nd:YAG laser oscillator;
the laser beam has an output power from 3.2 kW to 3.8 kW;
the zigzag pattern has a width between 4 mm and 6 mm;
the zigzag pattern has a pitch that is (a) equal to or less than 1 mm and (b) constant across at least a portion of the weld zone;
the laser beam is moved across the weld zone with a welding speed that is (a) from 150 mm sec −1 to 250 mm sec −1 and (b) constant across at least a portion of the weld zone;
the laser beam has a fusion zone having a fusion zone width that is larger than the pitch of the zigzag pattern; and
adjacent laser beam fusion zones in the zigzag pattern are partially overlapped.
2. The laser welding method of claim 1 , wherein, before irradiating the weld zone with the laser beam, the overlying and underlying metal sheets are separated by a gap having a width less than 1 mm.
3. The laser welding method of claim 1 , wherein at least a portion of the upper surface region of the underlying metal sheet that falls within the weld zone is separated from edges of the underlying metal sheet.
4. A laser welding method for lap-welding metal sheets, the method comprising:
providing an underlying metal sheet;
providing an overlying metal sheet that is positioned over a portion of the underlying metal sheet; and
irradiating a weld zone with a low heat input laser beam,
wherein:
the weld zone includes a selected edge of the overlying metal sheet and an upper surface region of the underlying metal sheet that is adjacent to the selected edge;
the laser beam is moved across the weld zone in a zigzag pattern;
the laser beam is oscillated by an Nd:YAG laser oscillator;
the laser beam has an output power from 3.2 kW to 3.8 kW;
the zigzag pattern has a pitch that is equal to or less than 1 mm;
the laser beam is moved across the weld zone with a welding speed that is from 150 mm sec −1 to 250 mm sec −1 ;
irradiating the weld zone results in the selected edge of the metal sheet being melted such that it becomes a filler metal for autogenous welding;
the laser beam has a fusion zone having a fusion zone width that is larger than the pitch of the zigzag pattern; and
adjacent laser beam fusion zones in the zigzag pattern are partially overlapped.
5. The laser welding method of claim 4 , wherein, before irradiating the weld zone with the laser beam, the overlying and underlying metal sheets are separated by a gap having a width less than 1 mm.
6. The laser welding method of claim 4 , wherein at least a portion of the upper surface region of the underlying metal sheet that falls within the weld zone is separated from edges of the underlying metal sheet.