Anti-frost coating and the application method thereof
View Patent ↗The present invention provides an anti-frost coating, which forms a coat having a hydrophilic and hydrophobic composite structure after being applied on a substrate, and contains a hydrophobic polymer and a hydrophilic polymer. The application method of the anti-frost coating comprises: dissolving the hydrophilic polymer and the hydrophobic polymer in a solvent to form a homogeneous solution, coating the solution on a substrate to form a film, drying and curing to form an anti-frost coat with a hydrophilic and super-hydrophobic composite structure including a super-hydrophobic surface layer and a hydrophilic inner layer. Water drips can roll off easily and the dust and impurities deposited on the surface can be easily removed. The anti-frost effect is desirable.
1. An application method of an anti-frost coating, comprising: dissolving a hydrophilic polymer and a hydrophobic polymer in an organic solvent to form a homogeneous solution, coating the homogeneous solution on a substrate to form a film, drying and curing the film to form the anti-frost coat with a hydrophilic and super-hydrophobic composite structure including a super-hydrophobic surface layer and a hydrophilic inner layer; wherein
the hydrophobic polymer is one of polyacrylate, polyolefin and fluorine containing polyacrylate or their mixture; or a copolymer of acrylate and fluorine containing acrylate;
the hydrophilic polymer is sodium polyacrylate, polyacrylic acid, poly(2-hydroxypropyl methacrylate) or their mixture; or a copolymer of two or more of sodium acrylate, acrylic acid and 2-hydroxyethyl methacrylate;
the organic solvent is one or more of dioxane, xylene, N,N-dimethyl formamide, N,N-dimethyl acetamide and methanol; and
the drying and curing pressure is 10-1000 Pa, the super-hydrophobic refers to a water contact angle greater than 150°.
2. The method according to claim 1 , wherein the hydrophilic polymer and the hydrophobic polymer are dissolved in a same organic solvent at 60-130° C.
3. The method according to claim 1 , wherein the drying and curing temperature is 20-60° C.
4. The method according to claim 1 , the acrylate is butyl acrylate, methyl methacrylate, or their mixture;
the fluorine containing acrylate is hexafluorobutyl acrylate, perfluorodecoyloxyl ethyl acrylate, or their mixture;
the polyacrylate is poly(methyl acrylate), poly(methyl methacrylate), poly(butyl acrylate) or their mixture;
the fluorine containing polyacrylate is poly(hexafluorobutyl acrylate), poly(perfluorodecoyloxyl ethyl acrylate) or their mixture; and
the polyolefin is polypropylene.