Easy-flowing polycarbonate/ABS moulding compositions with good mechanical properties and a good surface
The present invention relates to flame-resistant moulding compositions of polycarbonates and graft polymers which, in addition to good flow properties, have very good mechanical properties and a particularly good, trouble-free surface. These moulding compositions are suitable in particular for injection moulding uses for mouldings with thin wall thicknesses and high-gloss surfaces. The thermoplastic moulding compositions according to the invention comprise A) 65.0 to 82.0 parts by wt. of at least one aromatic polycarbonate, B) 4.0 to 11.0 parts by wt. of at least one graft polymer, C) 14.0 to 24.0 parts by wt. of at least one phosphorus-containing flameproofing agent, wherein the sum of the parts by weight of components A to C adds up to 100 parts by weight and the total content of the polymer which is formed from the grafting monomers or is added in the free form and is not bonded chemically to the graft base is less than 2.0 wt. %, based on the total moulding composition.
1. A flame-resistant, thermoplastic moulding composition comprising
A) 65.0 to 82.0 parts by wt. of at least one aromatic polycarbonate,
B) 4.0 to 11.0 parts by wt. of at least one graft polymer of
B.1) 5 to 95 parts by weight of a mixture of
B.1.1) 50 to 95 parts by wt. of styrene, α-methylstyrene, styrene substituted on the nucleus by methyl, C 1 -C 8 -alkyl methacrylate, C 1 -C 8 -alkyl acrylate, or a mixture of these compounds and
B.1.2) 5 to 50 parts by wt. of acrylonitrile, methacrylonitrile, C 1 -C 8 -alkyl methacrylates, C 1 -C 8 -alkyl acrylate, maleic anhydride, maleimides N-substituted by C 1 -C 4 -alkyl or phenyl or a mixture of these compounds on
B.2) 5 to 95 parts by wt. of a rubber-containing graft base,
C) 14.0 to 24.0 parts by wt. of at least one phosphorus-containing flameproofing agent, wherein the sum of the parts by weight of components A to C adds up to 100 parts by weight and wherein the total content of the polymer which is formed from grafting monomers or is added in free form and is not bonded chemically to the graft base is less than 2.0 wt. %, based on the total moulding composition.
2. A moulding composition composition according to claim 1 , wherein component
B) is present in an amount of from 5.0 to 10.0 parts by wt., and component
C) is present in an amount of from 15.0 to 20.0 parts by wt.
3. A moulding composition composition according to claim 1 , wherein component
B) is present in an amount of from 5.0 to 9.0 parts by wt., and component
C) is present in an amount of from 15.0 to 18.0 parts by wt.
4. A moulding composition according to claim 1 , comprising as rubbers of the graft base B.2 diene rubbers, acrylate rubbers, silicone rubbers or ethylene/propylene/diene rubbers.
5. A moulding composition according to claim 1 , wherein the at least one phosphorus-containing flameproofing agent (C) is the compound of formula (V)
wherein
R 1 , R 2 , R 3 and R 4 independently of each other denote in each case optionally halogenated C 1 to C 8 -alkyl, or C 5 to C 6 -cycloalkyl, C 6 to C 20 -aryl or C 7 to C 12 -aralkyl in each case optionally substituted by alkyl, and/or halogen,
n independently of each other denote 0 or 1
q denotes 0.80 to 5.00 and
X denotes a mono- or polynuclear aromatic radical having 6 to 30 C atoms, or a linear or branched aliphatic radical having 2 to 30 C atoms, which can be substituted by OH and can contain up to 8 ether bonds.
6. A moulding composition according to claim 5 , wherein X in the flameproofing agent is selected from the group consisting of phenyl, biphenylene and bisphenylisopropylidene.
7. A moulding composition according to claim 1 , wherein the total content of the polymer which is formed from grafting monomers or is added in free form and is not bonded chemically to the graft base is less than 1.5 wt. %, based on the total moulding composition.
8. A moulding M ulding composition according to claim 1 , additionally comprising at least one additive (D) selected from the group consisting of flameproofing synergists, antidripping agents, lubricants and mould release agents, nucleating agents, stabilizers, antistatics, dyestuffs, pigments, fillers and reinforcing substances.
9. A moulding composition according to claim 8 , wherein the additive D) is present in a content of 0.05 - 15.00 parts by wt.
10. A moulding composition according to claim 9 , wherein component D) comprises at least one fluorinated polyolefin in an amount of 0.1 to 1.0 part by wt., based on the total weight of the moulding composition.
11. A moulding composition according to claim 9 , wherein component D) comprises at least one mould release agent in an amount of 0.3 to 0.8 part by wt., based on the total weight of the moulding composition.
12. A moulding composition according to claim 9 , wherein component D) comprises at least one stabilizer in an amount of 0.06 to 0.2 part by wt., based on the total weight of the moulding composition, the stabilizer being selected from the group consisting of sterically hindered phenols and phosphites and mixtures thereof.
13. A method for the production of shaped articles comprising forming said shaped article from a moulding composition of claim 1 .
14. A shaped article produced from a moulding composition according to claim 1 .
15. A process for the preparation of a thermoplastic moulding composition of claim 1 comprising mixing components A to C and subjecting components A to C to melt compounding or melt extrusion at a temperature of from 200 to 330° C. after said mixing.
16. A flame-resistant, thermoplastic moulding composition comprising
A) 65.0 to 82.0 parts by wt. of at least one aromatic polycarbonate;
B) 5.0 to 9.0 parts by wt. of at least one graft polymer; and
C) 14.0 to 24.0 parts by wt. of at least one phosphorus-containing flameproofing agent of formula (V):
wherein
R 1 , R 2 , R 3 and R 4 independently of each other denote in each case optionally halogenated C 1 to C 8 -alkyl, or C 5 to C 6 -cycloalkyl, C 6 to C 20 -aryl or C 7 to C 12 -aralkyl in each case optionally substituted by alkyl, and/or halogen,
n independently of each other denote 0 or 1
q denotes 0.80 to 5.00 and
X denotes a mono- or polynuclear aromatic radical having 6 to 30 C atoms, or a linear or branched aliphatic radical having 2 to 30 C atoms, which can be substituted by OH and can contain up to 8 ether bonds;
wherein the sum of the parts by weight of components A to C adds up to 100 parts by weight and wherein the total content of the polymer which is formed from grafting monomers or is added in free form and is not bonded chemically to the graft base is less than 2.0 wt. %, based on the total moulding composition.
17. The thermoplastic moulding composition of claim 1 , having:
(i) weldline strength of at least 43 kJ/m 2 ;
(ii) Vicat temperature of about 87° C. to about 125° C.; and
(iii) melt viscosity (260° C./1,000s −1 ) of about 151 to about 221.
18. The thermoplastic moulding composition of claim 16 , having:
(i) weldline strength of at least 43 kJ/m 2 ;
(ii) Vicat temperature of about 87° C. to about 125° C.; and
(iii) melt viscosity (260° C./1,000s −1 ) of about 151 to about 221.
19. A moulding composition according to claim 1 , wherein the total content of the polymer which is formed from grafting monomers or is added in free form and is not bonded chemically to the graft base is less than 1.5 wt. %, based on the total moulding composition.
20. A moulding composition according to claim 16 , wherein the total content of the polymer which is formed from grafting monomers or is added in free form and is not bonded chemically to the graft base is less than 1.5 wt. %, based on the total moulding composition.