Thin-sheet glass substrate laminate and method of manufacturing the same
There is provided a thin-sheet glass substrate laminate which is approximately 100% impermeable to gas or vapor and has a high transparency and a thin thickness, and a method of manufacturing the same. A support is temporarily attached to one surface of a glass substrate after forming a pattern P on the one surface, the glass substrate is thinned by etching another surface of the glass substrate, a film base is temporarily attached to the etched another surface, the temporarily attached support is peeled off from the one surface of the glass substrate, the one surface from which the support is peeled off is laminated to a surface of a cover glass, and the temporarily attached film base is peeled off from the another surface.
1. A method of manufacturing a thin-sheet glass substrate laminate, comprising:
temporarily attaching a support to one surface of a glass substrate by an acid-resisting adhesive after forming a pattern on the one surface;
thinning the glass substrate by etching another surface of the glass substrate;
temporarily attaching a self-attachable slightly-adhesive film base to the etched another surface;
peeling off the temporarily attached support from the one surface of the glass substrate;
laminating the one surface from which the support is peeled off to a surface of a cover glass, a cover film or a display panel; and
peeling off the temporarily attached film base from the another surface.
2. A method of manufacturing a thin-sheet glass substrate laminate, comprising:
temporarily attaching a support to one surface of a glass substrate by an acid-resisting adhesive after forming a pattern on the one surface;
thinning the glass substrate by etching another surface of the glass substrate;
temporarily attaching a self-attachable slightly-adhesive film base to the etched another surface;
peeling off the temporarily attached support from the one surface of the glass substrate;
temporarily attaching a second film base to the one surface;
peeling off the temporarily attached film base from the another surface;
laminating a surface exposed by peeling off the film base to a surface of a cover glass, a cover film or a display panel; and
peeling off the temporarily attached second film base from the one surface.
3. The method of manufacturing a thin-sheet glass substrate laminate of claim 1 , wherein an FPC, or a COG substrate having an attached IC is mounted on the one surface of the glass substrate.
4. The method of manufacturing a thin-sheet glass substrate laminate of claim 1 , wherein the glass substrate is a large glass substrate, each of the film base and the second film base has a size corresponding to that of the large glass, and the glass substrate is cut into a product size after peeling off the support or after temporarily attaching the second film.
5. The method of manufacturing a thin-sheet glass substrate laminate of claim 2 , wherein an FPC, or a COG substrate having an attached IC is mounted on the one surface of the glass substrate.
6. The method of manufacturing a thin-sheet glass substrate laminate of claim 2 , wherein the glass substrate is a large glass substrate, each of the film base and the second film base has a size corresponding to that of the large glass, and the glass substrate is cut into a product size after peeling off the support or after temporarily attaching the second film.
7. The method of manufacturing a thin-sheet glass substrate laminate of claim 3 , wherein the glass substrate is a large glass substrate, each of the film base and the second film base has a size corresponding to that of the large glass, and the glass substrate is cut into a product size after peeling off the support or after temporarily attaching the second film.