Breathing sheet material having an adhesive coating layer and manufacturing method therefor
The invention relates to a breathing adhesive sheet material comprising a sheet layer having apertures and an adhesive coating layer with apertures corresponding to at least part of the apertures of said sheet layer, provided on one side of said sheet layer having apertures, wherein said apertures in said adhesive coating layer constitute portions of a substantially continuous adhesive coating layer separated there from by remaining adhered to a protective sheet layer upon removal thereof. The invention also relates to a composite sheet material comprising such adhesive sheet material with a removable protective sheet layer provided to separate portions from the continuous adhesive layer upon separation thereof from the adhesive sheet material. The invention also relates to a method for manufacturing such an adhesive sheet material comprising the steps of applying a layer of uncured adhesive material to a sheet layer having apertures and a layer of protective sheet material, and submitting the sheet layer having apertures, the layer of protective sheet material and the layer of uncured adhesive material to a curing operation, thereby causing the layer of adhesive material to preferentially adhere to the sheet layer having apertures outside the apertures, and to adhere to the protective sheet layer at said apertures.
1. A composite sheet material comprising a sheet layer having apertures, a continuous cured adhesive coating layer on said sheet layer; and a removable protective sheet layer adhering at least partially to said adhesive coating layer, wherein said adhesive coating layer shows a first adherence capacity A 1 towards the protective sheet layer and a second adherence capacity A 2 towards the sheet layer having apertures, said second adherence capacity A 2 being greater than said first adherence capacity A 1 ; the respective layers being arranged such that upon removal of said protective sheet layer, a portion of said adhesive coating layer remains on said protective sheet layer and the portion of said adhesive coating layer remaining adhered to said sheet layer includes apertures therein corresponding to at least a portion of the apertures of said sheet layer.
2. The composite sheet material of claim 1 , wherein said adhesive layer has a thickness between 50 μm and 1000 μm.
3. The composite sheet material of claim 1 , wherein said adhesive layer has a thickness between 100 μm and 500 μm.
4. The composite sheet material of claim 1 , wherein said protective sheet layer has a thickness ranging from about 0.01 mm to about 2 mm.
5. The composite sheet material of according to claim 1 , wherein said protective sheet layer has a thickness ranging from about from 0.02 mm to 0.6 mm.
6. The composite sheet material of claim 1 wherein said protective sheet material has a thickness ranging from 0.05 mm to about 1 mm.
7. The composite sheet material of claim 1 wherein said protective sheet material has a thickness ranging from 0.1 to 0.6 mm.
8. The composite sheet material of claim 1 wherein said adhesive layer is present on said sheet layer at a ratio of 10 to 500 g/m 2 .
9. The composite sheet material of claim 1 wherein said adhesive layer is present on said sheet layer at a ratio of 10 to 300 g/m 2 .
10. A method for manufacturing a sheet material comprising:
applying a continuous layer of uncured adhesive material to a layer of protective sheet material,
applying a sheet layer having apertures therein onto said continuous layer of uncured adhesive material to form a composite; and
submitting said composite to a curing operation for said adhesive material wherein, said adhesive material, when cured, and said protective sheet material show a first adherence capacity A 1 towards each other, and said sheet layer having apertures and said adhesive material, when cured, show a second adherence capacity A 2 towards each other, said second adherence capacity A 2 being greater than said first adherence capacity A 1 .
11. The method of claim 10 wherein said uncured adhesive material extends into said apertures of said sheet layer.
12. The method of claim 10 wherein said curing operation causes said layer of adhesive material to preferentially adhere to said area of the sheet layer which does not contain apertures.