Coating with antimicrobial agents
A coating with antimicrobial agents for use with medical devices. In one approach, a related method involves coating high temperature vulcanized silicone material with a room temperature vulcanized dispersion.
1. A method for coating a material with an antimicrobial agent, comprising:
mixing Octenidine Hydrochloride and an organic solvent with an uncured silicone polymer to form a coating mixture, wherein the mixing involves stirring until the coating mixture has a uniform color and consistency;
degassing the mixture to remove entrained bubbles; and
applying the coating mixture to a cured silicone polymer of a breast implant;
wherein the coating mixture is the most external layer without swelling the cured silicone polymer.
2. The method of claim 1 , wherein the uncured silicone polymer is an uncured RTV silicone elastomer.
3. The method of claim 2 , wherein the cured silicone polymer is a cured HTV silicone elastomer.
4. The method of claim 2 , wherein the cured silicone polymer is a cured RTV silicone elastomer.
5. The method of claim 1 , wherein the Octenidine Hydrochloride is present in an effective concentration to reduce bacterial colonization.
6. The method of claim 1 , further comprising providing the breast implant with extended antimicrobial efficacy.
7. A coating for a breast implant formed from a cured silicone elastomer, comprising:
an antimicrobial solution comprising Octenidine Hydrochloride and an organic solvent; and
an uncured RTV silicone elastomer;
wherein the antimicrobial solution and uncured RTV silicone elastomer form a mixture having a uniform color and consistency with entrained bubbles removed, and the mixture forms the most external layer of the breast implant without swelling the cured silicone elastomer.
8. The coating of claim 7 , wherein the uncured RTV silicone elastomer is dispersed in xylene.
9. A breast implant, comprising:
a body formed from a cured silicone elastomer; and
a coating having a uniform color and consistency formed from a xylene dispersion of RTV silicone elastomer and an antimicrobial solution including Octenidine Hydrochloride and an organic solvent with entrained bubbles removed, wherein the coating is applied at least partially to the body and forms the most external layer of the breast implant without swelling the cured silicone elastomer.
10. The breast implant of claim 9 , wherein the body is formed from a cured HTV silicone elastomer.
11. The breast implant of claim 9 , wherein the body is formed from a cured RTV silicone elastomer.
12. The breast implant of claim 9 , wherein the thickness of the coating applied to the body is controlled to achieve a desired concentration volume distribution of Octenidine Hydrochloride.