Method of manufacturing solid electrolytic capacitor
View Patent ↗A solid electrolytic capacitor having an even conductive polymer layer and a method of manufacturing the same are provided. The method of manufacturing a solid electrolytic capacitor includes the steps of forming a conductive polymer layer on an anode element by bringing a dispersion containing a conductive solid and a first solvent into contact with the anode element having a dielectric film formed thereon, washing the anode element with a second solvent higher in boiling point than the first solvent, in which the conductive solid can be dispersed, after the conductive polymer layer is formed, and drying the anode element washed with the second solvent at a temperature not lower than the boiling point of the first solvent and lower than the boiling point of the second solvent.
1. A method of manufacturing a solid electrolytic capacitor including an anode element having a dielectric film formed on its surface and a conductive polymer layer formed on said dielectric film, comprising the steps of:
adhering particles made of conductive polymer or aggregates made of conductive polymer onto said anode element by bringing a dispersion in which said particles made of conductive polymer or aggregates made of conductive polymer are dispersed in the first solvent into contact with said anode element having said dielectric film formed thereon;
washing said anode element onto which said particles made of conductive polymer or said aggregates made of conductive polymer are adhered with a second solvent higher in boiling point than said first solvent, in which said particles made of conductive polymer or said aggregates made of said conductive polymer can be dispersed; and
drying said anode element washed with said second solvent at a temperature not lower than the boiling point of said first solvent and lower than the boiling point of said second solvent.
2. The method of manufacturing a solid electrolytic capacitor according to claim 1 , wherein
in said step of adhering said particles made of conductive polymer or said aggregates made of conductive polymer onto said anode element, said anode element is dried after said dispersion is brought in contact with said anode element having said dielectric film formed thereon.
3. The method of manufacturing a solid electrolytic capacitor according to claim 1 , wherein
said step of adhering said particles made of conductive polymer or said aggregates made of conductive polymer onto said anode element is repeated a plurality of times, and a series of steps including the step of washing with a second solvent and the step of drying is performed at least once in between the repeated steps.
4. The method of manufacturing a solid electrolytic capacitor according to claim 1 , wherein
said first solvent is water or a solvent mixture mainly composed of water.
5. The method of manufacturing a solid electrolytic capacitor according to claim 1 , wherein
said second solvent has miscibility with said first solvent.
6. The method of manufacturing a solid electrolytic capacitor according to claim 1 , wherein
said second solvent has viscosity not higher than 100 mPas.