Process for forming a porous PVA scaffold using a pore-forming agent
The present invention relates to a process for forming a porous poly(vinyl alcohol) (PVA) scaffold using a pore-forming agent, comprising: mixing PVA with the pore-forming agent to form micropores in the PVA scaffold and using an easily decomposable pore-forming agent after the formation of the pores to improve convenience and reduce the processing time in manufacturing the porous PVA scaffold as well as to enable a pore size and porosity to be selected. A process for forming a porous PVA scaffold using a pore-forming agent according to the present invention includes heating to melt the PVA, cooling the melted PVA and mixing the PVA with a heat-decomposable pore-forming agent, repeating the freezing/thawing of the mixed PVA to cure the PVA mixture, and stirring the cured PVA mixture with a hydrochloric acid solution at a high temperature of 65° C. or more to produce foam.
1. A method for preparing a porous PVA scaffold using PVA and a pore-forming agent, comprising:
melting the PVA by heat;
cooling down the PVA and mixing the PVA with the pore-forming agent to form a PVA mixture;
repeatedly freezing/thawing the PVA mixture to form a cured PVA mixture; and
stirring the cured PVA mixture with a hydrochloric acid solution at a temperature of 65 to 100° C. to form the porous PVA scaffold.
2. The method as claimed in claim 1 , wherein the PVA has a concentration of 5 to 40% by weight.
3. The method as claimed in claim 1 , wherein the pore-forming agent is at least one selected from the group consisting of sodium hydrogen carbonate (NaHCO 3 ), ammonium hydrogen carbonate (NH 4 HCO 3 ), and a mixture thereof.
4. The method as claimed in claim 1 , wherein the PVA mixture includes the PVA and the pore-forming agent in a ratio of 1:1to 1:15.
5. The method as claimed in claim 1 , further comprising:
subsequent to melting the PVA by heat, using a microsieve to sort particles of the pore-forming agent into various particle sizes and retaining the particles having a defined range of particle size.
6. The method as claimed in claim 5 , wherein the defined range of particle size of the pore-forming agent is 100 to 300 μm.
7. The method as claimed in claim 1 , wherein a centrifugal machine is used to eliminate pores from the PVA while mixing the PVA with the pore-forming agent.
8. The method as claimed in claim 1 , further comprising:
subsequent to stirring the cured PVA mixture with the hydrochloric acid solution at a temperature of 65 to 100° C. to form the porous PVA scaffold, washing out the porous PVA scaffold with a base solution or distilled water.