Electrode material for vacuum circuit breaker and method of manufacturing the same
Atomized Cu—Cr alloy powder, 20 to 30 percent by weight of Thermite Cr powder and 5 percent by weight of electrolytic Cu powder are mixed together and undergo solid phase sintering treatment to form an electrode material for vacuum circuit breakers. The gross content of Cr of the electrode material is 30 to 50 percent by weight. In manufacturing the electrode material for vacuum circuit breakers, such powders are mixed together and then undergo compression molding to be formed into a compressed compact. The compressed compact is performed solid phase sintering at a temperature lower than the melting point of Cu in a non-oxidizing atmosphere to prepare a solid phase sintered body.
1. An electrode material for vacuum circuit breakers, the electrode material being prepared by solid phase sintering of atomized Cu—Cr alloy powder, 20 to 30 percent by weight of a metal Cr powder formed by thermite reduction and 5 percent by weight of electrolytic Cu powder,
wherein the gross content of Cr in the solid phase sintered body is 30 to 50 percent by weight.
2. A method of manufacturing an electrode material for vacuum circuit breakers, comprising the steps of:
mixing atomized Cu—Cr alloy powder, 20 to 30 percent by weight of a metal Cr powder formed by thermite reduction, and 5 percent by weight of electrolytic Cu powder to form a powder mixture;
compression molding the powder mixture to form a compressed compact; and
solid phase sintering the compressed compact in a non-oxidizing atmosphere at temperature below the melting point of Cu to form a solid phase sintered body, in which the gross content of Cr in the solid phase sintered body is 30 to 50 percent by weight.