Method for producing artificial bone and artificial bone produced by the method
A method for producing an artificial bone capable of accurate molding at a joined part with appropriate strength, in which electromagnetic waves or electron beams are irradiated to a layer of at least type of powder selected from metal biomaterials, ceramics for the artificial bone and plastic resins for the artificial bone based on image data corresponding to a shape of the artificial bone, thereby effecting sintering or melting, and the thus sintered layer or melted and solidified layer is laminated, such that a surface finish step is adopted that inner faces and/or outer faces of both ends and their vicinities configuring the joined part to a human bone part are polished by a rotating tool based on the image data and also irradiation of electromagnetic waves or electron beams at both ends and their vicinities constituting the joined part is set greater than that at other regions.
1. A method for producing an artificial bone comprising the steps of:
irradiating one of electromagnetic waves and electron beams to a layer of at least one type of powder selected from metal biomaterials, ceramics for an artificial bone and plastic resins for an artificial bone, based on image data corresponding to a shape of the artificial bone, thereby effecting at least one of sintering and melting,
laminating the thus sintered layer or the thus melted and solidified layer,
a surface finish step of polishing at least one of inner faces and outer faces of both ends and vicinities thereof configuring a joined part to a human bone part by a rotating tool based on the image data, and
said step of irradiating irradiates said both ends and their vicinities which configure the joined part, by said one of electromagnetic waves and electron beams, with a radiation dose which is set greater than a radiation dose for other regions by one of:
increasing an irradiation dose per unit area, and
prolonging an irradiation time in said step of irradiation,
to prevent fatigue and friction of said joined part.
2. The method for producing an artificial bone according to claim 1 , wherein
a maximum diameter of surface roughness based on the polishing by the rotating tool is 10 μm.
3. The method for producing an artificial bone according to claim 1 , further comprising:
a polishing step for polishing leading end faces of both ends by the rotating tool.
4. The method for producing an artificial bone according to claim 1 , further comprising the step of:
forming one of a meshed region and a pore aggregate region on at least some of a hollow peripheral wall along a longitudinal direction and the formed region is provided with a greater irradiation dose of said one of electromagnetic waves and electron beams than other regions.
5. The method for producing an artificial bone according to claim 1 , further comprising the step of:
using a CAD system to set image data corresponding to a shape of the artificial bone, and
using one of a CAD system and a CAM system to set at least one of the following:
irradiation dose per unit area, and
irradiation time of said one of electromagnetic waves and electron beams
in the artificial bone.
6. The method for producing an artificial bone according to claim 5 , further comprising the step of:
using the one of the CAD system and the CAM system to set at least one of the moving velocity and rotating velocity of the rotating tool in accordance with at least one of:
irradiation dose per unit area, and
irradiation time of said one of electromagnetic waves and electron beams.
7. The method for producing an artificial bone according to claim 1 , further comprising the step of:
forming at least some regions inside a peripheral wall along a longitudinal direction, besides both ends forming joint parts and positions of neighborhoods thereof, into a three dimensional meshed state.
8. The method for producing an artificial bone according to claim 1 , further comprising the step of:
setting a spot diameter to be irradiated with said one of electromagnetic waves and electron beams less than 100 μm.
9. The method for producing an artificial bone according to claim 1 , further comprising the step of:
adopting, as a laminated powder at both ends and vicinities thereof configuring the joined part, one of metal biomaterial powder and powder which is substantially composed of the metal biomaterial powder.
10. An artificial bone produced by the method for producing an artificial bone according to claim 1 .