Exhaust gas purification catalyst and method for purifying exhaust gas by using same
An exhaust gas purification catalyst of the present invention contains at least a precious metal coated with lanthanum-containing alumina. In at least one embodiment, it is possible to provide: an exhaust gas purification catalyst which can (i) have an increase in heat resistance, and (ii) inhibit the precious metal from being mixed in alumina and therefore inhibit the precious metal from forming a solid solution in combination with alumina; and a method for efficiently purifying, by use of the catalyst, an exhaust gas emitted from an internal-combustion engine.
1. An exhaust gas purification catalyst comprising:
a complex comprising a precious metal and a cerium oxide, wherein the complex is coated with a lanthanum-containing alumina, and
pores having a diameter of 160 nm to less than 1000 nm, which account for 5% to 20% of total pore volume of the catalyst.
2. The catalyst as set forth in claim 1 ,
further comprising pores having a diameter of less than 160 nm, which account for 70% to 90% of total pore volume of the catalyst.
3. The catalyst as set forth in claim 1 , wherein:
the catalyst is capable of maintaining the precious metal after the catalyst is exposed to an oxygen-excess gas having a temperature of 950° C. to 1000° C.
4. The catalyst as set forth in claim 3 , wherein:
an exposed surface area of the precious metal is reduced or unchanged when the catalyst is exposed to said gas.
5. The catalyst as set forth in claim 3 , wherein:
20% or less of the precious metal in atomic ratio is mixed into alumina to form a solid solution of alumina and the precious metal after the catalyst is exposed to said gas.
6. The catalyst as set forth in claim 1 , further comprising:
platinum, palladium or a combination thereof.
7. The catalyst as set forth in claim 1 , wherein:
a compound comprising the precious metal and the cerium oxide is formed at an interface between the precious metal and the cerium oxide in the complex.
8. The catalyst as set forth in claim 7 , wherein:
an amount of the cerium oxide contained in the complex is greater than an amount of the compound contained in the complex.
9. The catalyst as set forth in claim 1 , wherein:
an amount of the cerium oxide contained in the complex is 1% by mass to 30% by mass with respect to a total amount of the precious metal, the cerium oxide, lanthanum, and alumina in the catalyst.
10. The catalyst as set forth in claim 1 , wherein:
the catalyst is capable of maintaining the complex after the catalyst is exposed to an exhaust gas having a temperature of 950° C. to 1000° C., and wherein the exhaust gas is emitted from an internal-combustion engine.
11. The catalyst as set forth in claim 10 , wherein:
when the catalyst is exposed to said gas, an exposed surface area of the precious metal is reduced by a percentage of 0% to 87% with respect to an exposed surface area of the precious metal before the exposure of the catalyst to said gas.
12. The catalyst as set forth in claim 11 , wherein:
the catalyst is capable of absorbing 30% to 100% oxygen from said exhaust gas.
13. The catalyst as set forth in claim 1 , further comprising:
platinum, palladium, or a combination thereof, wherein the platinum, palladium or the combination thereof is not coated with lanthanum-containing alumina.
14. The catalyst as set forth in claim 1 , wherein:
the catalyst is supported on a three-dimensional structure.
15. The catalyst as set forth in claim 1 , further comprising:
a fire-resistant inorganic oxide.
16. The catalyst as set forth in claim 15 , wherein:
the fire-resistant inorganic oxide has a melting point of not less than 1000° C.
17. The catalyst as set forth in claim 1 , further comprising:
a cerium oxide, a ceria-zirconia composite oxide or a combination thereof, wherein the cerium oxide, the ceria-zirconia composite oxide or the combination thereof is not coated with lanthanum-containing alumina.
18. The catalyst as set forth in claim 1 , wherein:
the precious metal is rhodium.
19. A method for purifying an exhaust gas, the method comprising the step of:
exposing an exhaust gas purification catalyst as set forth in claim 1 to an exhaust gas emitted from an internal-combustion engine.
20. A method for purifying an exhaust gas, the method comprising the steps of:
(i) exposing an exhaust gas purification catalyst as set forth in claim 1 or 2 to a first exhaust gas having (I) a temperature in a range of 800° C. to 1000° C. and (II) an air-fuel ratio in a range of 10 to 18.6; and
(ii) exposing, after the step (i), the exhaust gas purification catalyst to a second exhaust gas which (1) has a temperature in a range of 0° C. to 750° C., and (2) is emitted from an internal-combustion engine.
21. A method for producing an exhaust gas purification catalyst as set forth in claim 1 , the method comprising the step of:
producing a gel in which a complex comprising a precious metal and a cerium oxide is coated with a lanthanum-containing alumina gel.
22. The method as set forth in claim 21 , the method further comprising the steps of:
turning, into a slurry, the gel in which the complex comprising the precious metal and the cerium oxide is coated with the lanthanum-containing alumina gel;
coating a three-dimensional structure with the slurry by washcoating; and
drying and baking the three-dimensional structure which is coated with the slurry.