Positive electrode active material sintered body for battery
The positive electrode active material sintered body for a battery of the present invention is a positive electrode active material sintered body for a battery satisfying the following requirements (I) to (VII): (I) fine particles in a positive electrode active material are sintered to constitute the sintered body; (II) a peak pore diameter which provides a maximum differential pore volume value in a pore diameter range of 0.01 to 10 μm in a pore distribution is 0.3 to 5 μm; (III) a total pore volume is 0.1 to 1 cc/g; (IV) an average particle diameter is not less than the peak pore diameter and not more than 20 μm; (V) any peak, which provides a differential pore volume value of not less than 10% of the maximum differential pore volume value, is not present on a smaller pore diameter side than the peak pore diameter in the pore distribution; (VI) a BET specific surface area is 1 to 6 m 2 /g; and (VII) a full width at half maximum of a strongest X-ray diffraction peak is 0.13 to 0.2.
1. A positive electrode active material sintered body for a battery satisfying the following requirements (I) to (VII):
(I) fine particles in a positive electrode active material and carbon particles are sintered to constitute the sintered body;
(II) a peak pore diameter which provides a maximum differential pore volume value in a pore diameter range of 0.01 to 10 μm in a pore distribution measured by a mercury porosimeter is 0.3 to 5 μm;
(III) a total pore volume measured by the mercury porosimeter is 0.1 to 1 cc/g;
(IV) an average particle diameter in laser diffraction/scattering particle diameter distribution measurement is not less than the peak pore diameter and not more than 5 μm;
(V) a peak, which provides a differential pore volume value of 10% or more of the maximum differential pore volume value and has a smaller pore diameter than the peak pore diameter in the pore distribution measured by the mercury porosimeter, is not present;
(VI) a BET specific surface area is 2 to 6 m 2 /g; and
(VII) a full width at half maximum of a strongest X-ray diffraction peak of the positive electrode active material sintered body is 0.13 to 0.2.
2. The positive electrode active material sintered body for the battery according to claim 1 , wherein the positive electrode active material is lithium manganate.
3. A composite material for a lithium battery containing the positive electrode active material sintered body for the battery according to claim 1 and a conductive material.
4. The composite material for the lithium battery according to claim 3 , wherein the conductive material is made of carbon.
5. A positive electrode for a lithium battery containing the composite material for the lithium battery according to claim 3 and a binder.
6. A lithium ion battery comprising a positive electrode containing the composite material for the lithium battery according to claim 3 and a binder.
7. The positive electrode active material sintered body for the battery according to claim 1 , wherein (III) a total pore volume measured by the mercury porosimeter is 0.3 to 1 cc/g.
8. A positive electrode active material sintered body for a battery satisfying the following requirements (I) to (IV) and (VI) to (VII):
(I) fine particles in a positive electrode active material and carbon particles are sintered to constitute the sintered body;
(II) a peak pore diameter which provides a maximum differential pore volume value in a pore diameter range of 0.01 to 10 μm in a pore distribution measured by a mercury porosimeter is 0.3 to 5 μm;
(III) a total pore volume measured by the mercury porosimeter is 0.1 to 1 cc/g;
(IV) an average particle diameter in laser diffraction/scattering particle diameter distribution measurement is not less than the peak pore diameter and not more than 5 μm;
(VI) a BET specific surface area is 2 to 6 m 2 /g; and
(VII) a full width at half maximum of a strongest X-ray diffraction peak of the positive electrode active material sintered body is 0.13 to 0.2.
9. The positive electrode active material sintered body for the battery according to claim 8 , wherein the positive electrode active material is lithium manganate.
10. A composite material for a lithium battery containing the positive electrode active material sintered body for the battery according to claim 8 and a conductive material.
11. The composite material for the lithium battery according to claim 10 , wherein the conductive material is made of carbon.
12. A positive electrode for a lithium battery containing the composite material for the lithium battery according to claim 10 and a binder.
13. A lithium ion battery comprising a positive electrode containing the composite material for the lithium battery according to claim 10 and a binder.
14. The positive electrode active material sintered body for the battery according to claim 8 , wherein (III) a total pore volume measured by the mercury porosimeter is 0.3 to 1 cc/g.