Dental curable composition and composite resin using the same
The present invention provides a dental curable composition exhibiting both excellent light diffusion and excellent transparency, and having high mechanical strength and surface smoothness and gloss after polishing as a cured product as well as good handling properties as a paste. The present invention is a dental curable composition including: a polymerizable monomer (A) having a refractive index of 1.52 to 1.58 after polymerization; inorganic particles (B) having a refractive index of 1.43 to 1.50; and inorganic particles (C) having a refractive index of 1.52 to 1.58. The inorganic particles (B) are aggregates of inorganic fine particles having an average primary particle size of 2 to 50 nm, and the content of the inorganic particles (B) is 0.1 to 10% by weight.
1. A dental curable composition comprising:
a polymerizable monomer (A) having a refractive index of 1.52 to 1.58 after polymerization;
inorganic particles (B) having a refractive index of 1.43 to 1.50; and
inorganic particles (C) having a refractive index of 1.52 to 1.58,
wherein the inorganic particles (B) are aggregates of inorganic fine particles having an average primary particle size of 2 to 50 nm, and the content of the inorganic particles (B) is 0.1 to 10% by weight,
and wherein the inorganic particles (C) comprise:
non-aggregated inorganic particles (C-I) having an average particle size of 0.1 to 1.0 μm, and
aggregated inorganic particles (C-II) having an average particle size of 1 to 20 μm and comprising silica-based fine particles having an average particle size of 2 to 50 nm and an oxide comprising at least one heavy metal
where a weight ratio between the inorganic particles (C-I) and the inorganic particles (C-II) is 1:4 to 4:1.
2. The dental curable composition according to claim 1 , wherein the inorganic particles (B) have an average particle size of 1.0 to 20 μm.
3. The dental curable composition according to claim 1 , wherein the inorganic particles (B) have a specific surface area of 50 to 400 m 2 /g and a pore volume of 0.05 to 1.5 mL/g.
4. The dental curable composition according to claim 1 , wherein a difference between the refractive index of the polymerizable monomer (A) after polymerization and the refractive index of the inorganic particles (C) is 0.03 or less.
5. The dental curable composition according to claim 1 , wherein a difference between the refractive index of the polymerizable monomer (A) after polymerization and the refractive index of the inorganic particles (B) is 0.05 or more.
6. The dental curable composition according to claim 1 , wherein the dental curable composition contains 8 to 40% by weight of the polymerizable monomer (A), 0.1 to 10% by weight of the inorganic particles (B), and 59.9 to 91.9% by weight of the inorganic particles (C).
7. The dental curable composition according to claim 1 , further comprising 1 to 10% by weight of inorganic ultrafine particles (D) having an average particle size of 5 to 50 nm.
8. A composite resin comprising the dental curable composition according to claim 1 .
9. The dental curable composition according to claim 1 , wherein polymerizable monomer (A) has a refractive index of 1.53 to 1.58 after polymerization.
10. The dental curable composition according to claim 1 , wherein polymerizable monomer (A) is a (meth)acrylic acid ester.
11. The dental curable composition according to claim 1 , wherein:
non-aggregated inorganic particles (C-I) have an average particle size of 0.2 to 0.7 μm, and
aggregated inorganic particles (C-II) have an average particle size of 2.0 to 15 μm and comprise silica-based fine particles having an average particle size of 5 to 35 nm and an oxide comprising at least one heavy metal
where the weight ratio between the inorganic particles (C-I) and the inorganic particles (C-II) is 1:3 to 3:1.
12. The dental curable composition according to claim 11 , wherein said at least one heavy metal is at least one selected from the group consisting of Al, Ti, Zr, Sr, Ba, La, Y, and Yb.
13. The dental curable composition according to claim 11 , wherein polymerizable monomer (A) has a refractive index of 1.53 to 1.58 after polymerization.
14. The dental curable composition according to claim 11 , wherein polymerizable monomer (A) is a (meth)acrylic acid ester.
15. The dental curable composition according to claim 14 , wherein the dental curable composition contains 8 to 40% by weight of the polymerizable monomer (A), 0.1 to 10% by weight of the inorganic particles (B), and 59.9 to 91.9% by weight of the inorganic particles (C).
16. The dental curable composition according to claim 15 , wherein said at least one heavy metal is at least one selected from the group consisting of Al, Ti, Zr, Sr, Ba, La, Y, and Yb.