Polypropylene composition with improved optics for film and moulding applications

1. Polypropylene composition comprising a propylene homopolymer or a propylene random copolymer having at least one comonomer selected from alpha-olefins with 2 or 4-8 carbon atoms and a comonomer content of not more than 8.0 wt %, wherein

the propylene homo- or copolymer is polymerized in the presence of a Ziegler-Natta catalyst, and

the polypropylene composition has a MWD of 3.5 to 6.0 and an MFR (2.16 kg/230° C.) of 4.0 g/10 min to 20.0 g/10 min determined according to ISO 1133,

characterized in that the polypropylene composition has not been subjected to a vis-breaking step,

has a haze of not more than 3.5%, determined according to ASTM D 1003/92, when cast into a film with a thickness of 50 micrometers,

has a clarity of at least 96.0%, determined according to ASTM D 1003/92, when cast into a film with a thickness of 50 micrometers, and

wherein the polypropylene composition has a tensile modulus in machine direction and in transverse direction of at least 450 MPa, determined according to ISO 527-3, when cast into a film with a thickness of 50 micrometers.

2. Polypropylene composition according to claim 1 wherein polypropylene composition has an amount of volatiles of 50 microgram C/g or less, determined according to VDA 277:1995.

3. Polypropylene composition according to claim 1 wherein the polypropylene composition has a sealing initiation temperature (SIT) of less than 135° C. and an interval between SIT and the sealing end temperature (SET) of at least 6° C. when cast into a film with a thickness of 50 micrometers.

4. Polypropylene composition according to claim 1 wherein the polypropylene composition has a gloss of at least 110%, determined according to DIN 67530 at an angle of 20° , when cast into a film with a thickness of 50 micrometers.

5. Polypropylene composition according to claim 1 wherein the polypropylene composition has a transparency of at least 94.0%, determined according to ASTM D 1003/92, when cast into a film with a thickness of 50 micrometers.

6. Polypropylene composition according to claim 1 wherein the polypropylene composition comprising a propylene random copolymer has a coefficient of friction (CoF) of not more than 0.115, determined according to DIN 53 375, three days after casting into a film with a thickness of 30 micrometers.

7. Polypropylene composition according to claim 1 wherein the polypropylene composition comprising a propylene homopolymer has a coefficient of friction (CoF) of not more than 0.250, determined according to DIN 53 375, 21 days after casting into a film with a thickness of 30 micrometers.

8. Polypropylene composition according to claim 1 wherein the comonomer is ethylene.

9. Polypropylene composition according to claim 1 wherein the propylene homo- or copolymer is obtainable by a process which comprises the polymerization of propylene monomers or propylene monomers and one or more types of comonomers in the presence of a high yield Ziegler-Natta olefin polymerization catalyst, which catalyst comprises a component in the form of particles having a predetermined size range which has been produced in a process comprising:

a. preparing a solution of a complex of a Group 2 metal and an electron donor by reacting a compound of said metal with said electron donor or a precursor thereof in an organic liquid reaction medium,

b. reacting said complex in solution with a compound of a transition metal to produce an emulsion the dispersed phase of which containing more than 50 mol % of the Group 2 metal in said complex,

c. maintaining the particles of said dispersed phase within the average size range of 5 to 200 micrometers by agitation in the presence of an emulsion stabilizer and

d. solidifying said particles, and recovering, optionally washing said particles to obtain said catalyst component.

10. A process for preparing a film wherein the polypropylene composition according to claim 1 is formed into a film, and wherein the polypropylene composition has not been subjected to a vis-breaking step.

11. A film comprising the polypropylene composition according to claim 1 .