Comminution process to produce precision wood particles of uniform size and shape with disrupted grain structure from wood chips

1. A process of comminution of wood chips (C) having a grain direction to produce a mixture of wood particles (P), wherein the wood chips are characterized by an average length dimension (L C ) as measured substantially parallel to the grain, an average width dimension (W C ) as measured normal to L C and aligned cross grain, and an average height dimension (H C ) as measured normal to W C and L C , and wherein the comminution process comprises the step of feeding the wood chips in a direction of travel substantially randomly to the grain direction through a counter rotating pair of intermeshing arrays of cutting discs (D) arrayed axially perpendicular to the direction of wood chip travel, wherein the cutting discs have a uniform thickness (T D ), and wherein at least one of L C , W C , and H C is greater than T D .

2. The process of claim 1 , wherein: T D >H C .

3. The process of claim 1 , wherein: T D ÷H C =4 or less.

4. The process of claim 3 , wherein: T D ÷H C =2 or less.

5. The process of claim 1 , wherein: 1/32 inch<T D <¾ inch.

6. The process of claim 1 , wherein the wood particles (P) are characterized by a length dimension (L P ) aligned substantially parallel to the grain, a width dimension (W P ) normal to L P and aligned cross grain, a height dimension (H P ) normal to W P and L P , L P ×H P dimensions defining two side surfaces characterized by substantially intact longitudinally arrayed fiber W P ×H P dimensions defining two cross-grain end surfaces characterized individually as aligned either normal to the grain or oblique to the grain, wherein a majority of the W P ×H P surfaces aligned oblique to the grain have end checking, and L P ×W P dimensions defining two parallel top and bottom surfaces.

7. The process of claim 5 , wherein a majority of the W P ×H P surfaces in the mixture of wood particles have end checking.

8. The process of claim 1 , wherein the mixture of wood particles is characterized by a substantially uniform size distribution profile as determined by the following protocol:

drying approximately 1000 g of the wood particles to constant weight at 110° F.;

pouring 400 g of the dried wood particles into a stacked screen assembly consisting of in a contiguous size-ordered array: a top 1-inch screen having 25.00 mm nominal sieve openings, a ½-inch screen having 12.50 mm nominal sieve openings, a ⅜-inch screen having 9.53 mm nominal sieve openings, a ¼-inch screen having 6.30 mm nominal sieve openings, a No. 4 screen having 4.74 mm nominal sieve openings, a No. 8 screen having 2.38 mm nominal sieve openings, a No. 10 screen having 2.00 mm nominal sieve openings, a No. 16 screen having 1.19 mm nominal sieve openings, a No. 20 screen having 0.84 mm nominal sieve openings, and a bottom pan;

shaking the stacked screen assembly for 10 minutes on a motorized tapping sieve shaker;

weighing the wood particles that are retained on each of the screens; and

determining that the wood particle mixture is characterized by a substantially uniform size range if the sum of the weights of wood particles retained on any contiguous five of the screens exceeds 320 g in total.

9. The process of claim 8 , wherein the sum of the weight of wood particles retained on any contiguous three of the screens exceeds 360 g in total.

10. The process of claim 1 , wherein the wood chips are further characterized by having a retained field moisture content of greater than 30% dry weight basis.