Suspension polymerization and foaming of water containing activated carbon-nano/microparticulate polymer composites
Synthesis of polystyrene and/or other thermoplastic polymers or polymer blends which, for example, contain activated carbon and/or bamboo carbon carrying a co-blowing agent such as water and/or at least one of 1-dimensional, 2-dimensional, and 3-dimensional nano/micro-materials in suspension polymerization without using the inverse emulsion process. CO 2 or other blowing agent based foaming processes such as extrusion, batch foaming, and injection molding may then be carried out to produce polymer foams that have low density, high-R value, bimodal structures, good mechanical properties, and high fire retardance.
1. A method of making a foamed polymer, said method comprising:
(a) preparing a foamable polymeric material precursor comprising:
(1) an aqueous suspension polymerization of a mixture comprising:
i. styrene or other monomer;
ii. solid polymeric material selected from the group consisting of polystyrene;
iii. foaming facilitating material having affinity for a suspension liquid, said foaming facilitating material selected from the group consisting of activated carbon, said foaming facilitating material adapted to absorb said suspension liquid in the absence of any surfactant-like molecules or polymers;
iv. selected additional material selected from the group consisting of 1-dimensional nano/micro-materials;
v. a suspension stabilizer selected from the group consisting of hydroxyethyl cellulose; and
vi. said suspension liquid selected from the group consisting of water; and
(2) a blowing agent selected from the group consisting of CO 2 , N 2 , hydrofluorocarbons, fluorocarbons, and mixtures thereof; and
(b) preparing a foamed polymer by a method selected from the group consisting of extrusion, injection molding, and batch foaming of said foamable polymeric material precursor.
2. A method according to claim 1 wherein said suspension liquid is absorbed by said foaming facilitating material before mixing with said styrene or other monomer or said polymeric material and starting suspension polymerization.
3. A method according to claim 1 wherein said solid polymeric material is present in an amount less than 65% by weight, based on a total amount of said styrene and said solid polymeric material.
4. A method according to claim 1 wherein said suspension liquid is present in an amount of from 10% to 400% by weight, based on said foaming facilitating material.
5. A method according to claim 1 wherein said foaming facilitating material is present in an amount of from about 20% to about 0.01% by weight, based on a total amount of said styrene and said solid polymeric material.
6. A method according to claim 1 wherein a ratio of said activated carbon to a total amount of said styrene and said polystyrene is in a range of from about 20% to about 0.01% by weight.
7. A method according to claim 1 wherein said foaming facilitating material is selected from the group consisting of activated carbon with an average particle size from 1 micrometer to 40 micrometers.
8. A method according to claim 1 wherein said additional material comprises a 1-dimensional nano/micro-material selected from the group consisting of smectite clays, organoclays, nanographites, graphite, graphene, and graphene oxide.
9. A method according to claim 1 wherein a ratio of said additional material to a total weight of said styrene and said solid polymeric material is in an amount less than 20% by weight.
10. A method of making a foamed polymer, said method comprising:
(a) preparing a foamable polymeric material precursor comprising:
(1) an aqueous suspension polymerization of a mixture comprising:
i. styrene or other monomer;
ii. solid polymeric material selected from the group consisting of polystyrene;
iii. foaming facilitating material having affinity for a suspension liquid, said foaming facilitating material selected from the group consisting of activated carbon, said foaming facilitating material adapted to absorb said suspension liquid in the absence of any surfactant-like molecules or polymers;
iv. selected additional material selected from the group consisting of 1-dimensional nano/micro-materials;
v. a suspension stabilizer selected from the group consisting of hydroxyethyl cellulose; and
vi. said suspension liquid selected from the group consisting of water; and
(2) a blowing agent comprising CO 2 ; and
(b) preparing a foamed polymer by a method selected from the group consisting of extrusion, injection molding, and batch foaming of said foamable polymeric material precursor.
11. A method according to claim 10 wherein said suspension liquid is absorbed by said foaming facilitating material before mixing with said styrene or other monomer or said polymeric material and starting suspension polymerization.
12. A method according to claim 10 wherein said solid polymeric material is present in an amount less than 65% by weight, based on a total amount of said styrene and said solid polymeric material.
13. A method according to claim 10 wherein said suspension liquid is present in an amount of from 10% to 400% by weight, based on said foaming facilitating material.
14. A method according to claim 10 wherein said foaming facilitating material is present in an amount of from about 20% to about 0.01% by weight, based on a total amount of said styrene and said solid polymeric material.
15. A method according to claim 10 wherein a ratio of said activated carbon to a total amount of said styrene and said polystyrene is in a range of from about 20% to about 0.01% by weight.
16. A method according to claim 10 wherein said foaming facilitating material is selected from the group consisting of activated carbon with an average particle size from 1 micrometer to 40 micrometers.
17. A method according to claim 10 wherein said additional material comprises a 1-dimensional nano/micro-material selected from the group consisting of smectite clays, organoclays, nanographites, graphite, graphene, and graphene oxide.
18. A method according to claim 10 wherein a ratio of said additional material to a total weight of said styrene and said solid polymeric material is in an amount less than 20% by weight.