Process for producing sulfide-based solid electrolyte
The invention provides a process for producing a sulfide-based solid electrolyte, the process having: a raw material composition preparation step for preparing a raw material composition containing at least sulfur (S), an adhesion inhibitor addition step for adding to the raw material composition an adhesion inhibitor that inhibits formation of adhered substances including the unreacted raw material composition, on the inner surface of a milling pot during mechanical milling, and a vitrification step for synthesizing sulfide-based glass by carrying out mechanical milling on the raw material composition to which the adhesion inhibitor has been added.
1. A process for producing a sulfide-based solid electrolyte, comprising:
preparing a raw material composition containing at least sulfur;
adding to the raw material composition an adhesion inhibitor that inhibits formation of adhered substances including the unreacted raw material composition on an inner surface of a milling pot during mechanical milling, the adhesion inhibitor being an alkane that is liquid at normal temperature; and
synthesizing sulfide-based glass by carrying out mechanical milling on the raw material composition to which the adhesion inhibitor has been added; and
baking the sulfide-based glass.
2. The production process according to claim 1 , wherein the alkane is liquid at 25° C.
3. The production process according to claim 1 , wherein the number of carbon atoms of the alkane is 5 or more.
4. The production process according to claim 3 , wherein the number of carbon atoms of the alkane is 6 or more.
5. The production process according to claim 4 , wherein the alkane that is liquid at normal temperature is n-heptane.
6. The production process according to claim 1 , wherein the boiling point of the alkane is 60 to 300° C.
7. The production process according to claim 6 , wherein the boiling point of the alkane is 80 to 200° C.
8. The production process according to claim 1 , wherein the water concentration in the adhesion inhibitor is 100 ppm or less.
9. The production process according to claim 1 , wherein the amount of adhesion inhibitor is 50 to 1000 parts by weight with respect to 100 parts by weight of the raw material composition.
10. The production process according to claim 1 , wherein the raw material composition further contains Li.
11. The production process according to claim 1 , wherein the raw material composition contains at least Li 2 S and P 2 S 5 .
12. The production process according to claim 11 , wherein the molar ratio of Li 2 S to P 2 S 5 is 68:32 to 74:26.
13. The production process according to claim 12 , wherein the molar ratio of Li 2 S to P 2 S 5 is 70:30.
14. The production process according to claim 1 , wherein the mechanical milling is milling that uses a planetary ball mill.