Surface modification for enhanced silanation of ceramic materials
A coated medical implant, such as a coated dental component, is provided, the coated medical implant including a substrate surface formed of a material comprising available hydroxyl groups and a silicon oxide coating layer chemisorbed on the substrate surface. A method for the preparation of such coated implants is also provided, the method involving application of the silicon oxide coating layer to the substrate surface by chemical vapor deposition. A dental structure is also provided, which includes a first dental component having a substrate surface formed of a material comprising available hydroxyl groups; a silicon oxide coating layer chemisorbed on the substrate surface; a silane coupling agent overlying and covalently attached to the silicon oxide layer; a dental cement overlying and coupled to the silane coupling agent; and a second dental component having a surface bonded to the dental cement.
1. A medical implant constructed of refractory metal oxide and having a surface and a silicon oxide coating layer chemisorbed on said surface, wherein the silicon oxide layer is deposited by chemical vapor deposition, and wherein the refractory metal oxide comprises zirconia.
2. The medical implant of claim 1 , wherein the medical implant is a dental component selected from the group consisting of dental implants, crowns, bridges, fillings, veneers, inlays, onlays, endodontic devices, and orthodontic brackets.
3. The medical implant of claim 1 , wherein the medical implant is a dental component, and further comprising a silane coupling agent covalently attached to the silicon oxide layer.
4. The medical implant of claim 3 , wherein the silane coupling agent is a selected from the group consisting of 3-methacryloyloxypropyltrimethoxysilane, (3-trimethoxysilylpropylmethacrylate), 3-acryloyloxypropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, N-[3-(trimethoxysilyl)propylethylenediamine], 3-mercaptopropyltrimethoxysilane, bis-[3-(triethoxysilyl)propyl]polysulfide, and combinations thereof.
5. The medical implant of claim 3 , further comprising an overlying dental cement coupled to the silane coupling agent.
6. The medical implant of claim 5 , wherein the dental cement is selected from the group consisting of polymer-based adhesives, cements, resin-modified glass ionomers, and combinations thereof.
7. The medical implant of claim 5 , wherein the cement is covalently bonded to the silane coupling agent.
8. The medical implant of claim 1 , wherein the thickness of the silicon oxide layer is between about 0.1 and about 50 nm.
9. The medical implant of claim 1 , wherein the thickness of the silicon oxide layer is less than about 30 nm.
10. The medical implant of claim 1 , wherein the thickness of the silicon oxide layer is less than about 10 nm.
11. A dental structure, comprising:
a first dental component constructed of a refractory metal oxide and having a surface, wherein the refractory metal oxide comprises zirconia;
a silicon oxide coating layer chemisorbed on the surface, wherein the silicon oxide layer is deposited by chemical vapor deposition;
a silane coupling agent overlying and covalently attached to the silicon oxide layer;
a dental cement overlying and coupled to the silane coupling agent; and
a second dental component having a surface bonded to the dental cement.
12. The dental structure of claim 11 , wherein one of the first and second dental components is selected from the group consisting of dental implants, crowns, bridges, fillings, veneers, inlays, onlays, endodontic devices, and orthodontic brackets.
13. The dental structure of claim 11 , wherein the silane coupling agent is a selected from the group consisting of 3-methacryloyloxypropyltrimethoxysilane, (3-trimethoxysilylpropylmethacrylate), 3-acryloyloxypropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, N-[3-(trimethoxysilyl)propylethylenediamine], 3-mercaptopropyltrimethoxysilane, bis-[3-(triethoxysilyl)propyl]polysulfide, and combinations thereof.
14. The dental structure of claim 11 , wherein the dental cement is selected from the group consisting of polymer-based adhesives, cements, resin-modified glass ionomers, and combinations thereof.
15. The dental structure of claim 11 , wherein the thickness of the silicon oxide layer is between about 0.1 and about 50 nm.
16. The dental structure of claim 11 , wherein the thickness of the silicon oxide layer is less than about 30 nm.
17. The dental structure of claim 11 , wherein the thickness of the silicon oxide layer is less than about 10 nm.
18. The dental structure of claim 11 , wherein the surface of the second dental component is constructed of a material selected from the group consisting of natural tooth, metal, porcelain fused to metal, porcelain, ceramic, resin, and combinations thereof.
19. A method of preparing the surface of a medical implant for silanation, comprising:
providing a medical implant constructed of refractory metal oxide comprising zirconia; and
applying a silicon oxide coating layer to the surface of the medical implant by chemical vapor deposition.
20. The method of claim 19 , wherein the application step comprises contacting the surface with one or more gaseous silicon-based precursors and water vapor.
21. The method of claim 20 , wherein the silicon-based precursor is selected from the group consisting of tetrachlorosilane (SiCl 4 ), tetrafluorosilane (SiF 4 ), tetrabromosilane (SiBr 4 ), trichlorosilane (HSiCl 3 ), trifluorosilane (HSiF 3 ), tribromosilane (HSiBr 3 ), hexachlorodisilane (Si 2 Cl 6 ), hexachlorodisiloxane (Si 2 Cl 6 O), and combinations thereof.
22. The method of claim 19 , wherein the medical implant is a dental component and the method further comprises reacting the silicon oxide coating layer of the dental component with a silane coupling agent.
23. The method of claim 22 , wherein the silane coupling agent is selected from the group consisting of 3-methacryloyloxypropyltrimethoxysilane, (3-trimethoxysilylpropylmethacrylate), 3-acryloyloxypropyltrimethoxysilane, 3-isocyanatopropyltriethoxysilane, N-[3-(trimethoxysilyl)propylethylenediamine], 3-mercaptopropyltrimethoxysilane, bis-[3-(triethoxysilyl)propyl]polysulfide, and combinations thereof.
24. The method of claim 22 , further comprising coupling the silane coupling agent to a dental cement.
25. The method of claim 24 , wherein the dental cement is selected from the group consisting of polymer-based adhesives, cements, resin-modified glass ionomers, and combinations thereof.
26. The method of claim 24 , further comprising bonding the dental component to another substrate with the dental cement.
27. The method of claim 19 , wherein the thickness of the silicon oxide coating layer introduced in the applying step is less than about 10 nm.
28. The method of claim 19 , wherein the thickness of the silicon oxide coating layer introduced in the applying step is less than about 30 nm.
29. The method of claim 19 , wherein the method further comprises roughening the substrate surface prior to said applying step.
30. The method of claim 19 , wherein the method further comprises treating the substrate surface with oxygen-containing plasma prior to said applying step.