Conjugated diene polymer, process for producing conjugated diene polymer, conjugated diene polymer composition and process for producing conjugated diene polymer composition
The present invention provides a conjugated diene polymer, a method for producing a conjugated diene polymer, a conjugated diene polymer composition and a method for producing a conjugated diene polymer composition. The conjugated diene polymer is a conjugated diene polymer having a conjugated diene-based monomer unit and a group of the formula (I), wherein assuming the whole area of the molecular weight distribution curve obtained by gel permeation chromatography as 100%, the peak area of the molecular weight peak at the lowest molecular weight side is not less than 50%: wherein R 1 and R 2 represent independently a hydrocarbon group, hydrocarbon oxy group or hydroxyl group, m represents an integer of 0 to 10, and A 1 represents a polar functional group free of an active hydrogen atom.
1. A method for producing a conjugated diene polymer composition, comprising steps 1, 2 and 3:
step 1: polymerizing a monomer containing a conjugated diene in a hydrocarbon solvent in the presence of an alkali metal catalyst to obtain a conjugated diene polymer having at its end an alkali metal derived from the catalyst,
step 2: adding a silicon compound of the formula (IV):
wherein R 6 , R 7 , and R 8 represent independently a hydrocarbon group having 1 to 4 carbon atoms or a hydrocarbon oxy group having 1 to 4 carbon atoms, at least one of R 6 , R 7 , and R 8 is a hydrocarbon oxy group having 1 to 4 carbon atoms, n represents an integer of 0 to 10, and A 2 represents a group of formula (II):
wherein R 3 and R 4 represent independently a hydrocarbon group having 1 to 6 carbon atoms optionally having a nitrogen atom, oxygen atom or silicon atom, and R 3 and R 4 may be connected to form a cyclic structure, to the hydrocarbon solution of the conjugated diene polymer, to modify the conjugated diene polymer with the silicon compound, and
step 3: mixing the conjugated diene polymer obtained in step 2 and silica,
wherein in step 2, the feed amount of the silicon compound of the formula (IV) is 0.1 to 10 mol per mol of the alkali metal of the alkali metal catalyst used in the step 1, and the feed rate of the silicon compound of the formula (IV) is not less than 6 mmol/sec/m 3 per unit volume of the hydrocarbon solution and per unit time.
2. The method according to claim 1 , wherein all of R 6 , R 7 and R 8 in the formula (IV) represent a hydrocarbon oxy group having 1 to 4 carbon atoms.
3. The method according to claim 1 , wherein, in the step 3, silica is added in an amount of 10 to 150 parts by weight per 100 parts by weight of the conjugated diene polymer obtained in the step 2.
4. The method according to claim 2 , wherein, in the step 3, silica is added in an amount of 10 to 150 parts by weight per 100 parts by weight of the conjugated diene polymer obtained in the step 2.
5. The method according to claim 1 , wherein all of R 6 , R 7 and R 8 in the formula (IV) represent a hydrocarbon oxy group having 1 to 4 carbon atoms.
6. The method according to claim 1 , wherein, in the step 3, silica is added in an amount of 10 to 150 parts by weight per 100 parts by weight of the conjugated diene polymer obtained in the step 2.
7. The method according to claim 5 , wherein, in the step 3, silica is added in an amount of 10 to 150 parts by weight per 100 parts by weight of the conjugated diene polymer obtained in the step 2.