Water-proof sound-transmitting membrane, method for producing water-proof sound-transmitting membrane, and electrical appliance using the membrane
A water-proof sound-transmitting membrane 10 includes a polytetrafluoroethylene porous membrane 1 and has a surface density of 1 to 20 g/m 2 . The polytetrafluoroethylene porous membrane 1 includes a first porous layer 1 a , and a second porous layer 1 b stacked on and integrated with the first porous layer 1 a by a binding force acting between polytetrafluoroethylene matrices.
1. A method for producing a water-proof sound-transmitting membrane, comprising the steps of:
extrusion-molding a paste containing a polytetrafluoroethylene fine powder and a processing aid forming a molded sheet;
stretching the sheet as a molded product of the paste or a sheet obtained by roll-pressing the molded product of the paste, in a first direction at a lower temperature than a melting point of polytetrafluoroethylene;
stacking a plurality of the stretched sheets;
stretching the stacked sheets in a second direction intersecting with the first direction at a lower temperature than the melting point of polytetrafluoroethylene; and
firing the stacked sheets at a temperature equal to or higher than the melting
point of polytetrafluoroethylene so that the stacked sheets are integrated with each other by a binding force acting between polytetrafluoroethylene matrices, the steps being performed in this order;
wherein stretching ratios at which the sheets are stretched in the first direction and the second direction, before firing are adjusted so that the water-proof sound-transmitting membrane has a surface density of 1 to 20 g/m 2 .
2. A method for producing a water-proof sound-transmitting membrane, comprising the steps of:
extrusion-molding a paste containing a polytetrafluoroethylene fine powder and a processing aid;
stretching biaxially an unfired sheet as a molded product of the paste or an unfired sheet obtained by roll-pressing the molded product of the paste, at a lower temperature than a melting point of polytetrafluoroethylene;
stacking a plurality of the stretched sheets; and
firing the stacked sheets at a temperature equal to or higher than the melting point of polytetrafluoroethylene so that the stacked sheets are integrated with each other by a binding force acting between polytetrafluoroethylene matrices, the steps being performed in this order; wherein stretching ratios of the sheets are adjusted so that the water-proof sound-transmitting membrane has a surface density of 1 to 20 g/m 2 .