Photopolymerizable flexographic printing elements for printing with UV inks

1. A process for flexographic printing with UV inks, which comprises

A) mounting at least one flexographic printing form onto a printing cylinder, wherein the at least one flexographic printing form is obtained by a process for producing a flexographic printing form for printing with UV inks which comprises

i) illuminating a photopolymerizable relief-forming layer with actinic light in accordance with an image and developing the illuminated, photopolymerizable relief-forming layer or

ii) illuminating the entire area of the photopolymerizable, relief-forming layer and engraving a printing relief into the illuminated photopolymerizable relief-forming layer using a laser,

wherein a photopolymerizable flexographic printing element is used,

B) transferring a UV ink to the at least one flexographic printing form with an inking unit,

C) transferring the UV ink from the at least one flexographic printing form to a print substrate by rotating the printing cylinder and the UV ink on the print substrate, and

D) curing the print substrate with UV radiation,

wherein the photopolymerizable flexographic printing element comprises at least

A) a dimensionally stable support and

B) a photopolymerizable, relief-forming layer comprising at least

1) from 40 to 90% by weight of a thermoplastic-elastomeric block copolymer comprising at least one block which consists essentially of alkenylaromatics and at least one block which consists essentially of 1,3-dienes,

2) from 1 to 20% by weight of ethylenically unsaturated monomers,

3) from 0.1 to 5% by weight of photoinitiator and

4) from 1 to 40% by weight of at least one plasticizer,

where the amounts are in each case based on the total amount of all components of the photopolymerizable relief-forming layer, and

wherein the at least one plasticizer comprises from 1 to 40% by weight of at least one cyclohexanepolycarboxylic ester of the general formula R 1 —(COOR 2 ) n where

n is 2, 3 or 4,

R 1 represents an n-valent cyclohexane radical, and

R 2 represents, independently of one another, a linear, branched or cyclic, aliphatic hydrocarbon radical having from 3 to 20 carbon atoms.

2. The process as claimed in claim 1 , wherein the process is carried out by narrow web printing and wherein the printing cylinder has a length of not more than 60 cm and a diameter of from 5 to 15 cm.

3. The process as claimed in claim 1 , wherein the UV ink comprises at least one acrylic ester of polyether polyols as monomer.

4. The process as claimed in claim 1 , wherein the UV ink comprises at least one monomer selected from the group consisting of ethoxylated tripropylene glycol diacrylate, ethoxylated trimethylolpropane triacrylate, dipropylene glycol diacrylate and tripropylene glycol diacrylate.

5. The process as claimed in claim 1 , wherein the plasticizer is a cyclohexane-1,2-dicarboxylic ester of the formula R 1 —(COOR 2 ) 2 .

6. The process as claimed in claim 1 , wherein R 2 is a linear, branched or cyclic, aliphatic hydrocarbon radical having from 6 to 12 carbon atoms.

7. The process as claimed in claim 1 , wherein the plasticizer is diisononyl cyclohexane-1,2-dicarboxylate.

8. The process as claimed in claim 2 , wherein the thermoplastic-elastomeric block copolymers comprise at least one styrene-isoprene block copolymer having a styrene content of from 10 to 30% by weight.

9. The process as claimed in claim 8 , wherein the thermoplastic-elastomeric block copolymers are radial styrene-isoprene block copolymers.

10. The process as claimed in claim 1 , wherein the thermoplastic-elastomeric block copolymers are at least two different styrene-isoprene block copolymers having a styrene content of in each case from 10 to 25% by weight, with one of the two block copolymers comprising a polyisoprene block having a 1,2-vinyl group content of at least 20%.

11. The process as claimed in claim 1 , wherein the amount of ethylenically unsaturated monomers is from 5 to 20% by weight.

12. The process as claimed in claim 1 , wherein at least one monomer having two ethylenically unsaturated groups is used.