Bearing grease composition
View Patent ↗A grease for use in fluid bearings can be made by combining a synthetic oil and a paraffinic wax. The grease can adhere to polymeric surfaces on bearings such as PTFE and can improve service life in high speed bearings such as those used in electric motors.
1. A high speed bearing grease composition comprising:
more than 50% by volume of an oil fraction, wherein the oil fraction has a complex viscosity between 0.003 Pa s and 0.05 Pa s at 40 deg C.;
more than 10% by volume of a paraffin wax, wherein the paraffin wax has a melting point in the range between 75 deg C. and 125 deg C.; and
more than 5% hydrocarbon based oil stabilizer by volume, the oil stabilizer having a higher viscosity than the oil fraction, wherein the hydrocarbon based oil stabilizer comprises at least one alkanes from the group of C12 to C22, C23, C26, C27, and C28 alkanes, wherein the high speed bearing grease composition is essentially free of metallic soaps and polyurea.
2. The high speed bearing grease composition of claim 1 , wherein the oil fraction comprises a polyalphaolefin formed from monomers of C 6 , C 7 , C 8 , C 9 , C 10 , C 11 , C 12 , and/or C 16 α-olephins.
3. The high speed bearing grease composition of claim 2 , wherein the polyalphaolefin has a D-445 viscosity of less than 100 cSt at 100° C.
4. The high speed bearing grease composition of claim 1 , wherein the hydrocarbon based oil stabilizer comprises an extreme pressure additive.
5. The high speed bearing grease composition of claim 1 , wherein the grease exhibits an ASTM D5483 oxidation induction time at 210° C. of greater than 5 minutes.
6. The high speed bearing grease composition of claim 1 , wherein the grease exhibits an ASTM D5483 oxidation induction time at 210° C. of greater than 30 minutes.
7. The high speed bearing grease composition of claim 1 , wherein the composition is essentially free of metallic soaps and polyurea.
8. The high speed bearing grease composition of claim 1 , wherein the oil fraction is essentially free of polybutylene.
9. An electric motor comprising the high speed bearing of claim 1 .
10. A bearing grease composition comprising:
more than 60% by volume of an oil fraction comprising a hydrocarbon; wherein the oil fraction has a complex viscosity at 100° C. from 0.05 Pa-s to 0.003 Pa-s,
more than 10% by volume of a paraffin wax, wherein the paraffin wax has a melting point in the range of 75° C. to 125° C.; and
more than 5% hydrocarbon based oil stabilizer by volume, the oil stabilizer having a higher viscosity than the oil fraction, wherein the hydrocarbon based oil stabilizer comprises at least one alkanes from the group of C12 to C22, C23, C26, C27, and C28 alkanes,
wherein the dynamic viscosity of the bearing grease is 10 times greater at 40° C. than at 70° C.,
wherein the high speed bearing grease composition is essentially free of metallic soaps and polyurea.
11. The bearing grease of claim 10 wherein the hydrocarbon based oil stabilizer comprises an extreme pressure additive.
12. The bearing grease of claim 10 wherein the paraffin wax has a melting point in the range of 75° C. to 125° C.
13. The bearing grease of claim 10 wherein the hydrocarbon further comprises a polyalphaolefin.
14. The bearing grease of claim 13 wherein the polyalphaolefin has a D-445 viscosity greater than 10 cSt at 40° C.
15. A high speed bearing grease composition comprising:
more than 60% and less than 70% synthetic hydrocarbon by volume, wherein the synthetic hydrocarbon comprises a polyalphaolefin having a D-445 viscosity of less than 100 cSt at 100° C.;
more than 15% paraffin wax by volume, wherein the paraffin wax has a melting point in the range of 75 to 125° C.; and
more than 5% hydrocarbon based oil stabilizer by volume, wherein the hydrocarbon based oil stabilizer comprises at least one alkanes from the group of C12 to C22, C23, C26, C27, and C28 alkanes, wherein the high speed bearing grease composition is essentially free of metallic soaps and polyurea.
16. The high speed bearing grease composition of claim 15 , wherein the synthetic hydrocarbon comprises a polyalphaolefin formed from monomers of C 6 , C 7 , C 8 , C 9 , C 10 , C 11 , C 12 , and/or C 16 α-olephins.
17. The high speed bearing grease composition of claim 15 , further comprising a petroleum based oil stabilizer.
18. The high speed bearing grease composition of claim 15 , wherein the grease exhibits an ASTM D5483 oxidation induction time at 210° C. of greater than 5 minutes.