Nickel-cobalt-manganese multi-element lithium ion battery cathode material with dopants and its methods of preparation
The present invention discloses a high compact density nickel-cobalt-manganese multi-element lithium ion battery cathode material with dopants and methods of its preparation. A preparation method of this battery cathode material is as follows: (A) preparing a nickel-cobalt-manganese multi-element intermediate with dopants by co-precipitation or chemical synthesis; (B) preparing a mixture by mixing said multi-element intermediate with a lithium salt; (C) pre-treating the said mixture, then adding into it polyvinyl alcohol and mixing uniformly; (D) pressing the resulting material into lumps, calcining the lumps at 800˜950° C., cooling after its removal from the furnace, crushing, passing through a 400 mesh sieve; (E) calcining the resulting power at 700˜800° C., cooling after its removal from the furnace, crushing and sieving to obtain a product. The lithium battery cathode material obtained using the above-described method has the formula LiNi x Co y Mn z M (1-x-y-z) O 2 . The cathode material has non-agglomerated single crystal particles. The material has a particle size ranging from 0.6˜30 μm, a compact density of 3.5˜3.7 g/cm 3 , and an initial discharge capacity of 150˜165 mAh/g, with excellent cycling and safety performance.
1. A method of preparing a nickel-cobalt-manganese multi-element lithium ion battery cathode material, comprising the steps of:
(1) preparing a nickel-cobalt-manganese multi-element intermediate, comprising:
dissolving salts of nickel, cobalt, and manganese in water to obtain an aqueous solution;
adding one or more salts selected from the group consisting of a molybdenum salt, a chromium salt, a germanium salt, an indium salt, a strontium salt, a tantalum salt, a magnesium salt, and a salt of a rare earth element to the aqueous solution;
stirring the solution to dissolve the salts,
wherein the resulting solution has a total molar concentration of metal elements of 0.8-1.3 mol/L, and a molar ratio of Ni:Co:Mn=(1.89-3.06):(1.5-2.1):(1-1.2), wherein a total mass percentage of molybdenum, chromium, germanium, indium, strontium, tantalum, magnesium or rare earth elements is 0.11%-0.3% of a total mass of nickel, cobalt, and manganese,
adding the above-described metal salt solution at a speed of 5-30 mL/min at a temperature in the range of 40° C. to 70° C. into an alkaline solution having polyethylene glycol, NaOH, and NH 3 , or into an oxalate solution having polyethylene glycol to obtain a reaction solution;
stirring the reaction solution for 1-2 h, then letting stand for 1-4 h;
filtering the reaction solution to obtain a solid;
washing the solid with deionized water to obtain a solid having a mass percentage of alkali metal in the solid of less than 0.01%;
drying the solids after washing at 105° C.-120° C. for 3-5 h to obtain the nickel-cobalt-manganese multiple-element intermediate;
(2) mixing the multi-element nickel-cobalt-manganese intermediate with a lithium salt uniformly according to a ratio of Li:(Ni+Co+Mn)=1.05-1.1:1 to obtain a first mixture;
grinding the first mixture for 2-8 h,
pre-treating the grinded for 2 h at 500° C.-550° C.;
adding polyvinyl alcohol into the pre-treated material, mixing evenly, and pressing the resulting mixture into lumps, wherein the mass percentage of the added polyvinyl alcohol is 0.98%-2% of the total mass of nickel, cobalt, and manganese;
(3) placing the material in lumps into a furnace, calcining the material in lumps at 800° C.-950° C. for 15-23 h, removing said material from the furnace, cooling it to 45° C.−5° C., crushing said material and passing it through a 400 mesh sieve;
(4) calcining the material that passes through a 400 mesh sieve at 700° C.-820° C. for 6-8 h, removing from the furnace, cooling to 45° C.-55° C., crushing the material, passing it through a 400 mesh sieve,
wherein the material obtained in step (4) comprises non-agglomerated single-grain particles and has a compact density of 3.5-3.7 g/cm 3 , the particles has a diameter of 0.6-30 μm and a chemical formula of LiNi x Co y Mn z M (1-x-y-z) O 2 wherein M is one or more of molybdenum, chromium, germanium, indium, strontium, tantalum, magnesium, or rare earth elements, the values of x, y, z are: 0.37≦x≦0.55, 0.27≦y≦0.35, 0.17<z<0.22, a content of M is 0.11%-0.3% of a total mass of nickel, cobalt, and manganese.
2. The method of claim 1 , characterized in that: the intermediate step of making the nickel-cobalt-manganese employing an amount of polyethylene glycol having a mass percentage of 0.4%-1.52% of the total mass of nickel, cobalt, and manganese.
3. The method of claim 1 , characterized in that the alkaline solution of NaOH and NH 3 has a pH value larger than 8.
4. The method of claim 1 or claim 3 , characterized in that the amount of alkaline solution mixture is 1.04-1.1 times the stoichiometric value calculated based on a reaction equation.
5. The method of claim 1 , characterized in that the oxalate solution has a molar concentration of 0.8-1.2 mol/L of ammonium or potassium oxalate.
6. The method of claim 1 or claim 5 , characterized in that the amount of oxalate solution is 1.05-1.1 time the stoichiometric value calculated based on a chemical reaction equation.
7. The method of claim 1 , characterized in that the salts for nickel, cobalt, manganese are selected from the group consisting of acetate salts, citrates, sulfates, and nitrates.