Stretched and foamed plastic container and method of producing the same
[Problems] To provide a foamed plastic container in which the cell diameters are varying along a gradient so will not to decrease the content protection performance, quite differently from the foamed cells distributed in the conventional foamed containers. [Means for Solution] The foamed plastic container has a container wall 10 formed by using a plastic material and in which foamed cells 1 are distributed, the lengths of the foamed cells in the surface direction of the container wall 10 decreasing from the outer surface of the container toward the inner surface thereof.
1. A stretched and foamed plastic container having a body wall equipped with a foamed region where foamed cells are distributed, wherein said foamed cells have a length gradient such that cell lengths in a stretched direction decrease from the foamed cells present on an outer surface side of the body wall toward the foamed cells present on an inner surface side of the body wall as compared in the same stretched direction and wherein the foamed cells positioned on an innermost surface side of the body wall have cell lengths in the stretched direction which are not larger than 0.5 times of the cell lengths of the foamed cells positioned on an outermost surface side of the body wall in the same stretched direction.
2. The stretched and foamed plastic container according to claim 1 , wherein the foamed cells positioned on the outermost surface side of the body wall have cell lengths not longer than 250 μm in an axial direction of the container.
3. The stretched and foamed plastic container according to claim 1 , wherein the stretched and foamed plastic container has a nozzle wall where no foamed cell is distributed.
4. The stretched and foamed plastic container according to claim 3 , wherein said nozzle wall has a smooth surface with a maximum height of roughness Pt (JIS-B-0601) of less than 10 μm.
5. The stretched and foamed plastic container according to claim 1 , wherein a portion of the body wall forms a foamed region where said foamed cells are distributed and another portion of the body wall forms a non-foamed region where no foamed cell is distributed.
6. The stretched and foamed plastic container according to claim 1 , wherein at least a portion of the body wall forms the foamed region therein where foamed cells are distributed, the foamed cells present in said foamed region being so distributed that the number of cells in a thickness direction differs in a surface direction.
7. The stretched and foamed plastic container according to claim 1 , wherein said container is formed by using a polyester, and when the outer surface of the body wall where the foamed cells are distributed is irradiated with an infrared ray at an angle of incidence of 45 degrees relative to the outer surface relying on a total reflection absorption method by using the infrared ray and a germanium prism, said outer surface exhibits such an infrared ray absorption property that an absorbency ratio R of the reflected beams defined by the following formula,
R=I 1340 /I 1409 (1)
wherein I 1340 is a peak absorbency corresponding to a longitudinal oscillation mode of CH 2 in a region of wave numbers of 1340±2 cm −1 , and
I 1409 is a reference peak absorbency in a region of wave numbers of 1409±2 cm −1 , is not larger than 1.30.
8. A stretched and foamed plastic container having a body wall equipped with a foamed region where foamed cells are distributed, wherein said container is formed by using a polyester, and when the outer surface of the body wall where the foamed cells are distributed is irradiated with an infrared ray at an angle of incidence of 45 degrees relative to the outer surface relying on a total reflection absorption method by using the infrared ray and a germanium prism, said outer surface exhibits such an infrared ray absorption property that an absorbency ratio R of the reflected beams defined by the following formula,
R=I 1340 /I 1409 (1)
wherein I 1340 is a peak absorbency corresponding to a longitudinal oscillation mode of CH 2 in a region of wave numbers of 1340±2 cm −1 , and
I 1409 is a reference peak absorbency in a region of wave numbers of 1409±2 cm −1 , is not larger than 1.30.