Aggregate-based mandrels for composite part production and composite part production methods
A method for forming a composite structure, using a mandrel that is later removed from the composite structure, involves production of a mandrel by depositing a particulate mixture, including an aggregate and a binder, into a mold and removing the mandrel from the mold. The mandrel may be treated while still in the mold by heating, curing with an agent, microwave energy, or by some combination thereof. Once finished, the mandrel can be used in manufacturing polymer and/or composite components. The mandrel can also be include materials that can be easily removed from the finished composite structure by water, shakeout, chemically dissolving, or by some combination thereof.
1. A mixture for use in manufacturing a mandrel, comprising: an organic binder material; an inorganic binder material; and an aggregate material, wherein organic binder material comprises polyvinylpyrollidone from 3% to 30% weight of the mixture, the inorganic binder material comprises alkali silicate from 3% to 30% weight of the mixture, and the aggregate material comprises cenospheres.
2. The mixture of claim 1 , wherein at least one of the organic binder material and the inorganic binder material is water soluble.
3. The mixture of claim 1 , wherein the mixture comprises from 3% to 20% weight alkali silicate.
4. The mixture of claim 3 , wherein the mixture comprises from 3% to 10% weight polyvinylpyrollidone, from 3% to 10% weight alkali silicate further comprises from 7% to 17% weight water and from 70% to 77% weight cenospheres.
5. The mixture of claim 1 , wherein the mixture comprises from 3% to 10% weight polyvinylpyrollidone.
6. The mixture of claim 1 , further comprising at least one additive selected from the group consisting of: anhydrous salts, solvents, alkaline hydroxides, surfactants, humidity resistant additives, collapsibility enhancers, preservatives, dyes, bulking agents, hot strength additives, flow enhancers, graphite, and refractory coatings.
7. The mixture of claim 6 , wherein the mixture contains less than 1% weight of the at least one additive.
8. The mixture of claim 1 , wherein at least one of the organic binder and the inorganic binder is microwave-curable.
9. The mixture of claim 1 , wherein the inorganic binder is acid gas-curable.
10. The mixture of claim 1 , wherein the aggregate material further comprises a material selected from the group consisting of: cenospheres, sand, fused silica, graphite, glass beads, and combinations thereof.
11. A mixture for use in manufacturing a mandrel, comprising: an organic binder material that is water soluble after curing; an inorganic binder material that curable by at least one of acid gas curing and microwave curing; and an aggregate material, materialmaterial, wherein organic binder material comprises polyvinylpyrollidone from 3% to 30% weight of the mixture, the inorganic binder material comprises alkali silicate from about 3% to 30% weight of the mixture, and the aggregate material comprises cenospheres.
12. The mixture of claim 11 , wherein the mixture comprises from 3% to 20% weight sodium silicate.
13. The mixture of claim 12 , wherein the mixture comprises from 3% to 10% weight polyvinylpyrollidone, from 3% to 10% weight sodium silicate, from 7% to 17% weight water, and from 70% to 77% weight cenospheres.
14. The mixture of claim 11 , wherein the mixture comprises from 3% to 10% polyvinylpyrollidone.
15. The mixture of claim 11 , further comprising at least one additive selected from the group consisting of: anhydrous salts, solvents, alkaline hydroxides, surfactants, humidity resistant additives, collapsibility enhancers, preservatives, dyes, bulking agents, hot strength additives, flow enhancers, and graphite.
16. The mixture of claim 15 , wherein the mixture contains less than 1% weight of the at least one additive.
17. A mixture for use in manufacturing a mandrel, consisting essentially of: from 3% to 10% weight polyvinylpyrollidone, from 3% to 10% weight alkali silicate, from 7% to 17% weight water, from 70% to 77% weight of an aggregate material, and at least one additive selected from the group consisting of: anhydrous salts, solvents, alkaline hydroxides, surfactants, humidity resistant additives, collapsibility enhancers, preservatives, dyes, bulking agents, hot strength additives, flow enhancers, and refractory coatings.
18. The mixture of claim 17 , wherein the aggregate material consists essentially of cenospheres.