This invention provides for a process of rapidly forming silk fibroin gelation through ultrasonication. Under the appropriate conditions, gelation can be controlled to occur within two hours after the ultrasonication treatment. Biological materials, including viable cells, or therapeutic agents can be encapsulated in the hydrogels formed from the process and be used as delivery vehicles.
1. A process of rapidly forming silk fibroin gelation, comprising exposing silk fibroin to a treatment comprising ultrasonication for a sufficient period of time to initiate gelation, wherein power of ultrasonic waves is 3 watts to 21 watts and wherein substantial silk fibroin gelation forms less than 24 hours after the ultrasonication treatment.
2. The process of claim 1 , wherein the silk fibroin gelation forms less than two hours after the ultrasonication treatment.
3. The process of claim 1 , wherein the silk fibroin undergoes gelation at a time period ranging from about five minutes to about two hours after the ultrasonication treatment.
4. The process of claim 1 , wherein the treatment further comprises a salt solution.
5. The process of claim 4 , wherein the salt solution comprises ions selected from the group consisting of potassium, calcium, sodium, magnesium, copper, zinc, and combinations thereof.
6. The process of claim 5 , wherein the salt is potassium, the salt concentration is less than 100 mM.
7. The process of claim 1 , wherein the silk fibroin is in the form of an aqueous solution having a pH that is about pH 4 or lower or is about pH 7.5 or higher.
8. A method of controlling gelation time of silk fibroin by contacting a silk fibroin solution with an ultrasonication treatment for a period of time to initiate gelation, wherein power of ultrasonic waves is 3 watts to 21 watts and wherein substantial silk fibroin gelation forms less than 24 hours after the ultrasonication treatment.
9. The method of claim 8 , wherein the silk fibroin gelation forms less than two hours after the ultrasonication treatment.
10. The method of claim 9 , wherein the silk fibroin undergoes gelation at a time period ranging from five minutes to two hours after the ultrasonication treatment.
11. The method of claim 8 , wherein the treatment further comprises a salt solution.
12. The method of claim 11 , wherein the salt solution comprises ions selected from the group consisting of potassium, calcium, sodium, magnesium, copper, zinc, and combinations thereof.
13. The method of claim 12 , wherein the salt is potassium, the salt concentration is less than 100 mM.
14. The method of claim 8 , wherein the silk fibroin is in the form of an aqueous solution having a pH that is about pH 4 or lower or is about pH 7.5 or higher.
15. A method of encapsulating at least one agent in silk fibroin, comprising:
(i)
a. contacting a silk fibroin solution with an ultrasonication treatment for a sufficient period of time to initiate gelation, wherein power of ultrasonic waves is 3 watts to 21 watts and wherein substantial silk fibroin gelation forms less than 24 hours after the ultrasonication treatment; and
b. introducing the agent(s) to the silk fibroin solution before substantial gelation occurs in the silk fibroin solution,
thereby forming a silk-fibroin encapsulated agent; or
(ii)
a. introducing the agent(s) to a silk fibroin solution; and
b. contacting a silk fibroin solution with an ultrasonication treatment for a sufficient period of time to initiate gelation, wherein power of ultrasonic waves is 3 watts to 21 watts and wherein substantial silk fibroin gelation forms less than 24 hours after the ultrasonication treatment,
thereby forming a silk-fibroin encapsulated agent.
16. The method of claim 13 , wherein the agent is a therapeutic agent or a biological material, or both.
17. The method of claim 13 , wherein the agent is selected from the group consisting of cells, proteins, peptides, nucleic acids, PNA, aptamers, antibodies, hormones, growth factors, cytokines, enzymes, antimicrobial compounds, small molecules, drugs, and combinations thereof.
18. The method of claim 17 , wherein said cell is a stem cell.
19. The method of claim 17 , wherein a cell growth medium is introduced into silk fibroin with the biological material.
20. The method of claim 17 , wherein the silk-fibroin encapsulated biological material is suitable for a biodelivery device.