Optical fiber preform, method of manufacturing optical fiber preform, and method of manufacturing optical fiber
A porous layer is formed by depositing a silica glass particle around a core rod. The porous layer is dehydrated. The dehydrated porous layer is sintered under a decreased pressure until the dehydrated porous layer becomes a translucent glass layer containing a closed pore. The translucent glass layer is vitrified under an ambient atmosphere including an inert gas other than a helium gas.
1. A method of manufacturing an optical fiber from an optical fiber perform that includes a core region and a cladding layer surrounding the core region comprising:
forming a porous layer by depositing a particle of a silica-based glass around a core rod made of a silica-based glass having the core region in a shape of a rod;
dehydrating the porous layer under at least one condition of a decreased pressure, an ambient atmosphere with an inert gas and a halogen gas, and an ambient atmosphere with an inert gas and a halogen-based compound gas;
sintering the dehydrated porous layer under a pressure equal to or lower than 2000 Pascals until the dehydrated porous layer becomes a glass layer containing a closed pore, the sintering being performed such that an average density of the porous layer becomes equal to or greater than 1.8 grams per cubic centimeter and less than 2.2 grams per cubic centimeter;
placing a portion of the glass layer in a heating furnace;
vitrifying only a leading edge of the glass layer and a portion of the glass layer extending in a longitudinal direction of the core rod on a side of starting a drawing, by heating the leading edge and the portion to form the optical fiber preform;
removing the optical fiber preform in which only the leading edge and the portion have been vitrified from the heating furnace;
inserting the optical fiber preform into a drawing furnace; and
drawing the optical fiber preform.
2. The method according to claim 1 , wherein
a method of heating the leading edge and the portion of the glass layer includes any one of heating by an electric furnace, heating by radiation of a flame of a flammable gas, and heating by radiation of a plasma flame.
3. The method according to claim 1 , wherein
the vitrifying includes tapering the leading edge simultaneously.
4. The method according to claim 1 , wherein a length from the leading edge to an end of the vitrified portion extending in the longitudinal direction of the core rod is 0.5 times to 1.0 times a diameter of a parallel portion of the portion of the glass layer.
5. The method according to claim 1 , wherein the leading edge and the portion are entirely placed in the drawing furnace at a start of the drawing.