Active material for lithium secondary battery, electrode for lithium secondary battery, lithium secondary battery, and method for producing the same
It is an object of the present invention to provide an active material for a lithium secondary battery having high discharge capacity and excellent in high rate discharge characteristics and a lithium secondary battery using the same. The active material for a lithium secondary battery containing a solid solution of a lithium-transition metal composite oxide having an α-NaFeO 2 type crystal structure and the lithium secondary battery using the same have features that the composition ratios of the metal elements contained in the solid solution satisfy Li 1+(x/3) Co 1−x−y−z Ni y/2 Mg z/2 Mn (2x/3)+(y/2)+(z/2) (x>0; y>0; z>0; x+y+z<1); the active material has an X-ray diffraction pattern capable of belonging to space group P 3 1 12 ; and the active material has discharge capacity exceeding 200 mAh/g. Further, in addition to the above-mentioned features, they have features that an intensity ratio between the diffraction peak of (003) plane and the diffraction peak of (114) plane measured by X-ray diffractometry is I (003) /I (114) ≧1.15 and/or the half width of the diffraction peak of (003) plane is 0.15° or less and the half width of the diffraction peak of (114) plane is 0.25° or less.
1. An active material for a lithium secondary battery comprising a solid solution of a lithium-transition metal composite oxide having an α-NaFeO 2 type crystal structure, wherein
the composition ratios of metal elements contained in the solid solution satisfy Li 1+(x/3) Co 1−x−y−z Ni y/2 Mg z/2 Mn (2x/3)+(y/2)+(z/2) (x>0; y>0; z>0; x+y+z<1);
the active material has an x-ray diffraction pattern capable of belonging to space group P3 1 12 or R3 − m; and
a peak intensity ratio between the diffraction peak intensity I (003) of (003) plane and the diffraction peak intensity I (114) of (114) plane or the diffraction peak intensity I (104) of (104) plane measured by x-ray diffractometry is I (003) /I (114) ≧1.15 or I (003) /I (104) ≧1.15.
2. The active material for a lithium secondary battery according to claim 1 , wherein the composition ratios of the metal elements contained in the solid solution of a lithium-transition metal composite oxide are 1/3<x<2/3; 0<y<2/3; and 0<z<0.3.
3. The active material for a lithium secondary battery according to claim 1 , wherein the valences of the respective elements constituting the solid solution of a lithium-transition metal composite oxide are Li 1+ , Mn 4+ , Ni 2+ , Co 3+ , and Mg 2+ .
4. The active material for a lithium secondary battery according to claim 1 , wherein the lithium-transition metal composite oxide has a crystallite size of 150 nm or larger.
5. The active material for a lithium secondary battery according to claim 1 , which has discharge capacity exceeding 200 mAh/g.
6. A method for producing the active material for a lithium secondary battery according to claim 1 , wherein the solid solution of a lithium-transition metal composite oxide is produced through the step of calcining at a calcining temperature of 920 to 1000° C.
7. A method for producing the active material for a lithium secondary battery according to claim 1 , comprising the step of producing the solid solution of a lithium-transition metal composite oxide by a coprecipitation method.
8. An electrode for a lithium secondary battery comprising the active material for a lithium secondary battery according to claim 1 .
9. A lithium secondary battery comprising the electrode for a lithium secondary battery according to claim 8 .
10. A method for producing the lithium secondary battery according to claim 9 employing a charging method where the positive electrode upon charge has a maximum reaching potential of 4.3 V (vs. Li/Li + ) or lower, the method comprising the step of:
charging the lithium secondary battery in such a manner that the potential of the electrode for a lithium secondary battery reaches at least a region appearing in a positive electrode potential range exceeding 4.3 V (vs. Li/Li + ) and 4.8 V (vs. Li/Li + ) or less and having a relatively plateau potential variation.
11. An active material for a lithium secondary battery comprising a solid solution of a lithium-transition metal composite oxide having an α-NaFeO 2 type crystal structure, wherein
the composition ratios of metal elements contained in the solid solution satisfy Li 1+(x/3) Co 1−x−y−z Ni y/2 Mg z/2 Mn (2x/3)+(y/2)+(z/2) (x>0; y>0; z>0; x+y+z<1);
the active material has an x-ray diffraction pattern capable of belonging to space group P3 1 12 or R3 − m; and
the half-width of the diffraction peak of (003) plane measured by x-ray diffractometry is 0.15° or less and the half-width of the diffraction peak of (114) plane or the diffraction peak of (104) plane measured by x-ray diffractometry is 0.25° or less.
12. The active material for a lithium secondary battery according to claim 11 , wherein the composition ratios of the metal elements contained in the solid solution of a lithium-transition metal composite oxide are 1/3<x<2/3; 0<y<2/3; and 0<z<0.3.
13. The active material for a lithium secondary battery according to claim 11 , wherein the valences of the respective elements constituting the solid solution of a lithium-transition metal composite oxide are Li 1+ , Mn 4+ , Ni 2+ , Co 3+ , and Mg 2+ .
14. The active material for a lithium secondary battery according to claim 11 , wherein the lithium-transition metal composite oxide has a crystallite size of 150 nm or larger.
15. The active material for a lithium secondary battery according to claim 11 , which has discharge capacity exceeding 200 mAh/g.
16. A method for producing the active material for a lithium secondary battery according to claim 11 , wherein the solid solution of a lithium-transition metal composite oxide is produced through the step of calcining at a calcining temperature of 920 to 1000° C.
17. A method for producing the active material for a lithium secondary battery according to claim 11 , comprising the step of producing the solid solution of a lithium-transition metal composite oxide by a coprecipitation method.
18. An electrode for a lithium secondary battery comprising the active material for a lithium secondary battery according to claim 11 .
19. A lithium secondary battery comprising the electrode for a lithium secondary battery according to claim 18 .
20. A method for producing the lithium secondary battery according to claim 19 employing a charging method where the positive electrode upon charge has a maximum reaching potential of 4.3 V (vs. Li/Li + ) or lower, the method comprising the step of:
charging the lithium secondary battery in such a manner that the potential of the electrode for a lithium secondary battery reaches at least a region appearing in a positive electrode potential range exceeding 4.3 V (vs. Li/Li + ) and 4.8 V (vs. Li/Li + ) or less and having a relatively plateau potential variation.