Method of activating an article of passive ferrous or non-ferrous metal prior to carburising, nitriding and /or nitrocarburising
A method of activating an article of passive ferrous or non-ferrous metal by heating at least one compound containing nitrogen and carbon, wherein the article is treated with gaseous species derived from the compound. The activated article can be subsequently carburized, nitrided or nitrocarburized in shorter time at lower temperature and resulting superior mechanical properties compared with non-activated articles and even articles of stainless steel, nickel alloy, cobalt alloy or titanium based material can be carburized, nitrided or nitrocarburized.
1. A method of case hardening an article of stainless steel, a nickel alloy, a cobalt alloy, a titanium based material or combinations thereof, the method comprising;
providing a heating apparatus having a first heating zone downstream of a second heating zone, the heating apparatus having a gas inlet and a gas outlet for providing a passage of gas through the heating apparatus,
heating the article in the first zone of the heating apparatus to a first temperature in a range of 185 to 500° C.,
heating in the second heating zone of the heating apparatus at least one compound containing nitrogen and carbon, said compound having a single, double, or triple carbon-nitrogen bond, which compound is liquid or solid at a temperature of 25° C. and a pressure of 1 bar, said compound hereinafter called an N/C compound, to a second temperature which is lower than the first temperature, and which is in a range of 135 to 450° C. for providing one or more gaseous species, and
establishing a passage of gas using a carrier gas that is non-oxidative to the article for contacting the article with the gaseous species to activate the article, and successively heating the article in the heating apparatus in the presence of the gaseous species to a carburizing, nitriding, or nitrocarburizing temperature which is at least as high as the first temperature and which is below 500° C.
2. The method according to claim 1 , wherein a difference between the first temperature and the second temperature is at least 50° C.
3. The method according to claim 1 , wherein the N/C compound is an amide.
4. The method according to claim 1 , wherein the N/C compound is selected from the group consisting of urea, acetamide, and formamide.
5. The method according to claim 1 , wherein the N/C compound is urea.
6. The method according to claim 1 , wherein the first temperature is in a range of 250 to 350° C.
7. The method according to claim 1 , wherein the second temperature is below 250° C.
8. The method according to claim 1 , wherein the second temperature is in a range of 135 to 170° C.
9. The method according to claim 1 , wherein the article is contacted with the gaseous species for at least one hour.
10. The method according to claim 1 , wherein the same N/C compound is used both for activation and for subsequent carburizing, nitriding or nitrocarburizing.
11. A method of case hardening an article of stainless steel, a nickel alloy, a cobalt alloy, a titanium based material or combinations thereof, the method comprising:
providing a heating apparatus having a doser;
heating the article in the heating apparatus to a first temperature in the range of 185 to 500° C.;
introducing at least one compound containing nitrogen and carbon, said compound having a single, double, or triple carbon-nitrogen bond, which compound is liquid or solid at a temperature of 25° C. and a pressure of 1 bar, said compound hereinafter called an N/C compound, into the heating apparatus by the doser;
allowing the N/C compound to vaporize to form a gaseous species and allowing the gaseous species to contact the article to activate the article;
successively heating the article in the heating apparatus in the presence of the gaseous species to a carburizing, nitridinq, or nitrocarburizinq temperature which is at least as high as the first temperature and which is below 500° C.
12. The method according to claim 11 , wherein the N/C compound is introduced into the heating apparatus by a carrier gas that is non-oxidative to the article.
13. The method according to claim 12 wherein the N/C compound is introduced continuously or discontinuously into the heating apparatus.
14. The method according to claim 11 , wherein the N/C compound is liquid.
15. The method according to claim 11 , wherein the first temperature is in a range of 350 to 500° C.
16. The method according to claim 11 , wherein the N/C compound is an amide.
17. The method according to claim 11 , wherein the N/C compound is selected from the group consisting of urea, acetamide, and foramide.
18. The method according to claim 11 , wherein the N/C compound is urea.
19. The method according to claim 11 , wherein the article is contacted with the gaseous species for at least one hour.
20. The method according to claim 11 , wherein the same N/C compound is used both for activation and for subsequent carburizing, nitriding or nitrocarburizing.