Coated abrasive grains, method and for the production thereof as well as the use thereof for producing abrasives

1. Abrasive grains selected from the group consisting of aluminum oxide, fused aluminum oxide, sintered aluminum oxide, alumina zirconia, silicon carbide, boron carbide, cubic boron nitride, diamond and mixtures thereof, the abrasive grains having a geopolymeric coating, the coating comprising a binder and a micro-particle inorganic powder, the binder comprising:

an aluminosilicate with a molar ratio of Al 2 O 3 to SiO 2 of 1:2 to 1:20,

sodium silicate, and

water,

wherein the precursor to the binder is a water-diluted base mixture of approximately 60 percent to approximately 90 percent by weight of water,

wherein the coating is applied directly to the abrasive grains, and

wherein the coated abrasive grains have an NTU-value ranging from 196 to 817.

2. The abrasive grains according to claim 1 , wherein the binder additionally comprises at least one complex alkaline fluoride.

3. The abrasive grains according to claim 2 , wherein the chemical composition of the precursor to the binder is approximately 5 to approximately 30 percent by weight of SiO 2 , approximately 1 to approximately 10 percent by weight of Al 2 O 3 and approximately 5 to approximately 15 percent by weight of alkaline fluoride.

4. The abrasive grains according to claim 1 , wherein the portion of the binder is approximately 0.01 to approximately 10.0 percent by weight, based on the untreated abrasive grain.

5. The abrasive grains according to claim 4 , wherein the binder is made up of approximately 0.005 to approximately 4.0 percent by weight of water glass, approximately 0.005 to approximately 4.0 percent by weight of water, approximately 0.0005 to approximately 1.0 percent by weight of aluminosilicate and approximately 0.001 to approximately 1.0 percent by weight of alkaline fluoride, in each case based on the untreated abrasive grain.

6. The abrasive grains according to claim 5 , wherein the aluminosilicate is chosen from at least one of the group consisting of metakaolins, flue ashes, slags, fine sands and activated clays.

7. The abrasive grains according to claim 6 , wherein the aluminosilicate comprises a product of reactive Al 2 O 3 and reactive SiO 2 , which was created in situ in response to coating said abrasive grains.

8. The abrasive grains according to claim 7 , wherein the aluminosilicate is a gel formed by polycondensation of reactive Al 2 O and reactive SiO 2 comprising a three-dimensional network of SiO 4 and AlO 4 tetrahedrons.

9. The abrasive grains according to claim 8 , wherein the at least one complex alkaline fluoride is chosen from the group Na 3 AlF 6 , K 2 NaAlF 6 , Na 2 SiF 6 , K 2 SiF 6 , NaBF 4 and KBF 4 .

10. The abrasive grains according to claim 9 , wherein the binder additionally comprises fillers and/or grinding additives, chosen from the group of sulfides, phosphates, carbonates, and/or halogenides, and/or sulfide, phosphate, carbonate and/or halogenide-containing complex compounds from the group of elements: Na, Li, K, Mg, Ca, Al, Mn, Cu, Sn, Fe, Ti, Sb and/or Zn.

11. The abrasive grains according to claim 10 , wherein the micro-particle inorganic powder is an oxide pigment.

12. The abrasive grains according to claim 11 , wherein the coating encompasses approximately 0.002 to approximately 5.0 percent by weight of micro-particle inorganic powder, based on the untreated abrasive grain.

13. The abrasive grains according to claim 12 , wherein the coating preferably encompasses approx. 0.1 to approximately 2.0 percent by weight of micro-particle inorganic powder, based on the untreated abrasive grain.

14. The abrasive grains according to claim 13 , wherein the binder is hardened when heated to a temperature of <400° C.

15. The abrasive grains according to claim 2 , wherein the portion of the binder is approximately 0.01 to approximately 10.0 percent by weight, based on the untreated abrasive grain.

16. The abrasive grains according to claim 3 , wherein the portion of the binder is approximately 0.01 to approximately 10.0 percent by weight, based on the untreated abrasive grain.

17. The abrasive grains according to claim 16 , wherein the binder is made up of approximately 0.005 to approximately 4.0 percent by weight of water, approximately 0.0005 to approximately 1.0 percent by weight of aluminosilicate and approximately 0.001 to approximately 1.0 percent by weight of alkaline fluoride, in each case based on the untreated abrasive grain.

18. The abrasive grains according to claim 2 , wherein the binder is made up of approximately 0.005 to approximately 4.0 percent by weight of water, approximately 0.0005 to approximately 1.0 percent by weight of aluminosilicate and approximately 0.001 to approximately 1.0 percent by weight of alkaline fluoride, in each case based on the untreated abrasive grain.

19. The abrasive grains according to claim 1 , wherein the aluminosilicate is chosen from at least one of the group consisting of metakaolins, flue ashes, slags, fine sands and activated clays.

20. The abrasive grains according to claim 19 , wherein the aluminosilicate comprises a product of reactive Al 2 O 3 , and reactive SiO 2 , which was created in situ in response to the coating reaction.

21. The abrasive grains according to claim 1 , wherein the aluminosilicate comprises a product of reactive Al 2 O 3 , and reactive SiO 2 , which was created in situ in response to the coating reaction.

22. The abrasive grains according to claim 21 , wherein the aluminosilicate is a gel formed by polycondensation of reactive Al 2 O and reactive SiO 2 comprising a three-dimensional network consisting of SiO 4 and AlO 4 tetrahedrons.

23. The abrasive grains according to claim 1 , wherein the aluminosilicate is a gel formed by polycondensation of reactive Al 2 O and reactive SiO 2 comprising a three-dimensional network consisting of SiO 4 and AlO 4 tetrahedrons.

24. The abrasive grains according to claim 23 , wherein the at least one complex alkaline fluoride is chosen from the group Na 3 AlF 6 , K 2 NaAlF 6 , Na 2 SiF 6 , K 2 SiF 6 , NaBF 4 and KBF 4 .

25. The abrasive grains according to claim 2 , wherein the at least one complex alkaline fluoride is chosen from the group Na 3 A1F 6 , K 2 NaAlF 6 , Na 2 SiF 6 , K 2 SiF 6 , NaBF 4 and KBF 4 .

26. The abrasive grains according to claim 1 , wherein the binder additionally comprises fillers and/or grinding additives, chosen from the group of sulfides, phosphates, carbonates, halogenides, and/or sulfide, phosphate, carbonate and/or halogenide-containing complex compounds from the group of elements: Na, Li, K, Mg, Ca, Al, Mn, Cu, Sn, Fe, Ti, Sb and/or Zn.

27. The abrasive grains according to claim 1 , wherein the micro-particle inorganic powder is an oxide pigment.

28. The abrasive grains according to claim 1 , wherein the coating encompasses approximately 0.002 to approximately 5.0 percent by weight of micro-particle inorganic powder, based on the untreated abrasive grain.

29. The abrasive grains according to claim 1 , wherein the coating preferably encompasses approximately 0.1 to approximately 2.0 percent by weight of micro-particle inorganic powder, based on the untreated abrasive grain.

30. The abrasive grains according to claim 1 , wherein the binder is hardened by heating it to a temperature of <400° C.

31. A method for producing abrasive grains according to claim 1 , comprising the steps:

wetting the abrasive grains with a binder in an intensive mixer;

adding a micro-particle inorganic powder to the wetted abrasive grains;

mixing the abrasive grains with the micro-particle inorganic powder until the powder is homogeneously distributed on the surface of the abrasive grains thereby coating said abrasive grains, and

heating the coating at a temperature of <400° C., which hardens the coating; wherein the binder comprises:

aluminosilicate with a molar ratio of Al 2 O 3 to SiO 2 of 1:2 to 1:20,

sodium silicate, and

water, and

the precursor to the binder is a water-diluted base mixture of approximately 60 percent to approximately 90 percent by weight of water.

32. The method according to claim 31 , wherein the binder additionally comprises at least one complex alkaline fluoride.

33. The method according to claim 31 , wherein the chemical composition of the precursor to the binder is approximately 5 to approximately 30 percent by weight of SiO 2 , approximately 1 to approximately 10 percent by weight of Al 2 O 3 and approximately 5 to approximately 15 percent by weight of alkaline fluoride is used.

34. The abrasive grains according to claim 1 , wherein the binder further comprises at least one complex alkaline fluoride selected from the group consisting of K 2 SiF 6 and Na 3 AlF 6 .