Method and apparatus for applying a Mid-IR graded-index microstructure to an optical fiber tip to achieve anti-reflective properties
A method and apparatus for applying a mid-IR graded microstructure to the end of an As2S3 optical fiber are presented herein. The method and apparatus transfer a microstructure from a negative imprint on a nickel shim to an As2S3 fiber tip with minimal shape distortion and minimal damage-threshold impact resulting in large gains in anti-reflective properties.
1. A method for preventing reflection losses in optical fibers, the method comprising:
heating an appropriately terminated As2S3 optical fiber tip to form a heated optical fiber tip;
flattening the heated optical fiber tip to form a flattened optical fiber tip;
heating the flattened optical fiber tip; and
imprinting a microstructure onto the flattened optical fiber tip.
2. The method of claim 1 , further comprising applying pressure to the heated As2S3 fiber tip against a substantially flat surface.
3. The method of claim 1 , further comprising applying pressure to the flattened As2S3 fiber tip against a negative imprinting surface.
4. The method of claim 2 , further comprising causing the pressure applied to the heated As2S3 fiber tip to be in the range of about 3,000 PSI to about 80,000 PSI.
5. The method of claim 3 , further comprising causing the pressure applied to the flattened As2S3 fiber tip to be in the range of about 3,000 PSI to about 80,000 PSI.
6. The method of claim 2 , further comprising causing the heated As2S3 fiber tip to be heated to a range of about 170° C. to about 270° C.
7. The method of claim 2 , further comprising causing the flattened As2S3 fiber tip to be heated to a range of about 170° C. to about 270° C.
8. The method of claim 3 , further comprising causing the imprinting surface to have a plurality of protrusions and recesses.
9. A method for preventing reflection losses in properly terminated As2S3 fibers, the method comprising:
securing a properly terminated As2S3 fiber into a ferrule, so that a tip of the properly terminated As2S3 fiber protrudes about 1 mm to 2 mm from the ferrule;
fastening the ferrule to a fixture;
lowering the fixture onto a heating surface, such that the heating surface transfers heat to the properly terminated As2S3 fiber tip without touching the properly terminated As2S3 fiber tip;
adjusting the orientation of the fixture with a hollow cylinder placed between the fixture and the heating surface to ensure perpendicularity of the properly terminated As2S3 fiber tip relative to the heating surface;
lowering the fixture so that the properly terminated As2S3 fiber tip contacts the heating surface;
replacing the heating surface with a hot imprinting surface;
lowering the fixture onto the hot imprinting surface, such that the hot imprinting surface transfers heat to the properly terminated As2S3 fiber tip without touching the properly terminated As2S3 fiber tip; and
lowering the fixture so that the properly terminated As2S3 fiber tip contacts the hot imprinting surface.
10. The method of claim 9 , further comprising applying a pressure of about 3,000 PSI to about 144,000 PSI to the properly terminated As2S3 fiber tip against the heating surface.
11. The method of claim 10 , further comprising applying a pressure of about 3,000 PSI to about 144,000 PSI to the properly terminated As2S3 fiber tip against the hot imprinting surface.
12. The method of claim 11 , further comprising removing the properly terminated As2S3 fiber tip from heating surface after a contact period of about 10 seconds to about 300 seconds.
13. The method of claim 11 , further comprising removing properly terminated As2S3 fiber tip from the hot imprinting surface after a contact period of about 10 seconds to about 300 seconds.
14. The method of claim 11 , wherein the step of lowering the fixture onto a heating surface includes lowering the properly terminated As2S3 fiber tip to within about 100 μm to about 200 μm of the heating surface.
15. The method of claim 11 , wherein the step of lowering the fixture onto the hot imprinting surface includes lowering the properly terminated As2S3 fiber tip to within about 100 μm to about 200 μm of the hot imprinting surface.