Silicone coating as a sealing layer for a decoration layer

1. A glass or glass ceramic article comprising:

a glass or glass ceramic substrate;

a decoration layer applied to at least some surface portions of the glass or glass ceramic substrate, the decoration layer is a cured sol-gel coating including first inorganic solid particles; and

a sealing layer is applied to at least portions of the decoration layer and to at least some surface portions of the glass or glass ceramic substrate without the decoration layer, the sealing layer is a cured silicone-based coating including second inorganic solid particles, the second inorganic solid particles comprising pigment particles, and the second inorganic solid particles being present in the sealing layer in a proportion that ranges from 10 to 70 wt. % of total weight of the sealing layer,

wherein the sealing layer comprises a coating selected from the group consisting of polysiloxane coating, a polysilsesquioxane coating, and any mixtures thereof.

2. The article as claimed in claim 1 , wherein the proportion ranges from 20 to 50 wt. % of total weight of the sealing layer.

3. The article as claimed in claim 1 , wherein the proportion ranges from 30 to 40 wt. % of total weight of the sealing layer.

4. The article as claimed in claim 1 , wherein the first inorganic solid particles comprise pigment particles, fillers, and any combinations thereof.

5. A glass or glass ceramic article comprising:

a glass or glass ceramic substrate;

a decoration layer applied to at least some surface portions of the glass or glass ceramic substrate, the decoration layer is a cured sol-gel coating including first inorganic solid particles; and

a sealing layer is applied to at least portions of the decoration layer and to at least some surface portions of the glass or glass ceramic substrate without the decoration layer, the sealing layer is a cured silicone-based coating including second inorganic solid particles, the second inorganic solid particles comprising pigment particles, and the second inorganic solid particles being present in the sealing layer in a proportion that ranges from 10 to 70 wt. % of total weight of the sealing layer,

wherein the first inorganic solid particles comprise pigment particles, fillers, and any combinations thereof, and

wherein the decoration layer further comprises solid lubricant.

6. A glass or glass ceramic article comprising:

a glass or glass ceramic substrate;

a decoration layer applied to at least some surface portions of the glass or glass ceramic substrate, the decoration layer is a cured sol-gel coating including first inorganic solid particles; and

a sealing layer is applied to at least portions of the decoration layer and to at least some surface portions of the glass or glass ceramic substrate without the decoration layer, the sealing layer is a cured silicone-based coating including second inorganic solid particles, the second inorganic solid particles comprising pigment particles, and the second inorganic solid particles being present in the sealing layer in a proportion that ranges from 10 to 70 wt. % of total weight of the sealing layer, wherein the sealing layer further comprises solid lubricant.

7. The article as claimed in claim 1 , wherein the decoration layer comprises, as a cured sol-gel binder, a metal oxide network.

8. The article as claimed in claim 7 , wherein the metal oxide network is a SiO 2 network.

9. The article as claimed in claim 7 , wherein the decoration layer further comprises solid lubricant and a material selected from the group consisting of pigment particles, fillers, and combinations thereof, the material being present in a ratio to the solid lubricant in a range from 10:1 to 1:1, in weight percentages.

10. The article as claimed in claim 1 , wherein the decoration layer further comprise a solid lubricant selected from the group consisting of graphite, alpha-boron nitride, molybdenum sulfide, and any combinations thereof.

11. The article as claimed in claim 1 , wherein the polysiloxane coating comprises a methyl-based polysiloxane coating or a polydimethylsiloxane coating.

12. The article as claimed in claim 1 , wherein the polysilsesquioxane coating comprises organic radicals selected from the group consisting of ethoxy, hydroxy groups, and combinations thereof.

13. The article as claimed in claim 1 , wherein the sealing layer comprises, as the pigment particles, particles selected from the group consisting of black pigments, spinels, effect pigments, and platelet-shaped pigments.

14. The article as claimed in claim 13 , wherein the sealing layer further comprises a solid lubricant.

15. The article as claimed in claim 1 , wherein the decoration layer has an L* value from 2 to 30 as measured through the glass or glass ceramic substrate.

16. The article as claimed in claim 1 , wherein the decoration layer has an L* value from 65 to 98 as measured through the glass or glass ceramic substrate.

17. The article as claimed in claim 1 , wherein the decoration layer has a temperature-stable Lab colorimetric locus that varies by not more than 1 when exposed to temperatures of not more than 450° C. for not more than 5 minutes, the colorimetric loci being measured through the glass or glass ceramic substrate.

18. A method for producing a glass or glass ceramic article, comprising:

mixing inorganic solid particles and a sol to form a decoration mixture;

applying the decoration mixture to at least some surface portions of a glass or glass ceramic substrate;

curing the decoration mixture to form a decoration layer;

mixing solid particles and a silicone-based coating solution to form a sealing mixture;

applying the sealing mixture to the glass or glass ceramic substrate coated with the decoration layer; and

curing the sealing mixture to form a sealing layer, wherein the sealing layer comprises a coating selected from the group consisting of a polysiloxane coating, a polysilsesquioxane coating, and a mixture thereof.

19. The method as claimed in claim 18 , wherein the inorganic solid particles comprise particles selected from the group consisting of pigment particles, fillers, and combinations thereof.

20. A method for producing a glass or glass ceramic article, comprising:

mixing inorganic solid particles and a sol to form a decoration mixture;

applying the decoration mixture to at least some surface portions of a glass or glass ceramic substrate;

curing the decoration mixture to form a decoration layer;

mixing solid particles and a silicone-based coating solution to form a sealing mixture;

applying the sealing mixture to the glass or glass ceramic substrate coated with the decoration layer; and

curing the sealing mixture to form a sealing layer,

wherein the inorganic solid particles comprise particles selected from the group consisting of pigment particles, fillers, and combinations thereof, and

wherein the decoration mixture further comprises solid lubricant.

21. The method as claimed in claim 20 , wherein the particles have a ratio of weight percentage to solid lubricant ranging from 10:1 to 1:1.

22. The method as claimed in claim 18 , wherein the solid particles comprise particles selected from the group consisting of black pigments, spinels, effect pigments, platelet-like pigments.

23. A method for producing a glass or glass ceramic article, comprising:

mixing inorganic solid particles and a sol to form a decoration mixture;

applying the decoration mixture to at least some surface portions of a glass or glass ceramic substrate;

curing the decoration mixture to form a decoration layer;

mixing solid particles and a silicone-based coating solution to form a sealing mixture;

applying the sealing mixture to the glass or glass ceramic substrate coated with the decoration layer; and

curing the sealing mixture to form a sealing layer,

wherein the solid particles comprise particles selected from the group consisting of black pigments, spinels, effect pigments, platelet-like pigments, and

wherein the sealing layer further comprises a solid lubricant.

24. The method as claimed in claim 18 , wherein the step of curing the sealing mixture to form the sealing layer comprises drying at temperatures above 200° C.