Resin compositions for extrusion coating
A composition of matter suitable for use in extrusion coating applications is disclosed. The composition comprises a blend of particular LLDPE with particular LDPE. The LLDPE has the following characteristics: a density in the range of from 0.89 g/cc to 0.97 g/cc; an MWD less than 2.8; a melt index (I 2 ) in the range of 4.0 to 25 g/10 min; a Comonomer Distribution Constant in the range of from greater than from 45 to 400; and a vinyl unsaturation of less than 0.12 vinyls per one thousand carbon atoms present in the backbone of the ethylene-based polymer composition. The LDPE has a melt index (I 2 ) in the range of 0.1 to 15 g/10 min, and has a melt strength which satisfies the inequality: Log Melt strength (cN)>1.14−0.6×Log I 2 (g/10 min,190° C.)
1. A composition of matter comprising:
c. from about 97 to about 50 percent by weight of the composition, of a Linear PE having
i. a density in the range of from 0.89 g/cc to 0.97 g/cc,
ii. an Mw/Mn less than 2.8
iii. a melt index (I 2 ) in the range of 4.0 to 25 g/10 min
iv. a Comonomer Distribution Constant in the range of from 45 to 400,
v. a vinyl unsaturation of less than 0.12 vinyls per one thousand carbon atoms present in the backbone of the ethylene-based polymer composition; and
d. from about 3 to about 50 percent by weight of the composition of a high pressure low density type polyethylene resin having a melt index (I 2 ) in the range of 0.1 to 15 g/10 min, and having a melt strength which satisfies the inequality
Log Melt strength (cN)>1.14−0.6×Log I 2 (g/10 min,190° C.)
wherein the MI of the composition of matter is in the range of from 4 g/10 minutes to 20 g/10 min.
2. The composition of matter of claim 1 wherein the Linear PE has an MWD of at least 1.8.
3. The composition of matter of claim 1 wherein the Linear PE has a density in the range of 0.905 to 0.93 g/cc.
4. The composition of matter of claim 1 wherein the Linear PE has an MWD in the range of 2.0 to 2.3.
5. The composition of matter of claim 1 wherein the Linear PE has a melt index of 8 to 15 g/10 min.
6. The composition of matter of claim 1 wherein the Linear PE has a Comonomer Distribution Constant of from 55 to 150.
7. The composition of matter of claim 1 wherein the Linear PE has a vinyl unsaturation in the range of from 0.01 to 0.08 vinyls per one thousand carbon atoms present in the backbone of the ethylene-based polymer composition.
8. The composition of matter of claim 1 wherein the Linear PE is further characterized by having a Long Chain Branching frequency (LCBf) of from 0.02 to 3 long chain branches per 1000 carbon atoms.
9. The composition of matter of claim 8 wherein the Linear PE has a Long Chain Branching frequency (LCBf) of from 0.02 to 0.5 long chain branches per 1000 carbon atoms.
10. The composition of matter of claim 1 wherein the Linear PE is further characterized by having a Zero Shear Viscosity Ratio (ZSVR) of at least 1.4.
11. The composition of matter of claim 1 wherein the Linear PE comprises from 97 to 60% by weight of the composition.
12. The composition of matter of claim 1 wherein the high pressure low density type polyethylene resin has a melt strength which satisfies the inequality Log Melt Strength (cN)>1.18−0.6×Log I 2 .
13. The composition of matter of claim 1 wherein the high pressure low density type polyethylene resin has a melt index in the range of 0.4 to 12 g/10 min.
14. The composition of matter of claim 1 wherein the MI of the composition of matter is in the range of from 4 g/10 minutes to 15 g/10 min.
15. The composition of matter of claim 1 wherein the MI of the composition of matter is in the range of from 7 g/10 minutes to 12 g/10 min.
16. A film made from the composition of matter of any of the preceding claims.
17. The film of claim 16 further comprising one or more additional layers.
18. The composition of matter of claim 1 further comprising one or more additional resin components.
19. The composition of matter of claim 1 further comprising one or more additives.
20. The composition of matter of claim 19 wherein the additive is selected from the group consisting of antioxidants, phosphites, cling additives, pigments, colorants, fillers, or combinations thereof.