Grafted pigment dispersing polymeric additive and paint employing the same with improved hiding
The present invention relates to a grafted pigment dispersing polymeric additive for opacifying pigments, prepared by polymerizing monomers in the presence of a polymeric pigment dispersant. The polymeric pigment dispersant has low molecular weight, high acid number and is dissolvable in alkali solution. When incorporated into paint compositions, hiding is improved with less opacifying pigments.
1. A grafted pigment dispersing polymeric additive comprising a polymeric pigment dispersant and a polymeric carrier grafted to each other, wherein the polymeric pigment dispersant has a weight average molecular weight of about 1,000 Daltons to about 20,000 Daltons and an acid number from about 150 to about 250 and wherein the polymeric pigment dispersant is soluble in an alkali solution, and
wherein the minimum film forming temperature (MFFT) of the polymeric carrier is greater than about 10° C. and less than about 130° C., and
wherein the grafted pigment dispersing polymeric additive is capable of adsorbing to an opacifying pigment, and
wherein the additive comprises particles having an average particle size in the range of about 75 nm to about 200 nm in diameter.
2. The grafted pigment dispersing polymeric additive of claim 1 , wherein the MFFT is greater than about 15° C.
3. The grafted pigment dispersing polymeric additive of claim 1 , wherein the MFFT is greater than about 20° C.
4. The grafted pigment dispersing polymeric additive of claim 1 , wherein the MFFT is less than about 100° C.
5. A grafted pigment dispersing polymeric additive comprising a polymeric pigment dispersant and a polymeric carrier grafted to each other, wherein the polymeric pigment dispersant has a weight average molecular weight of about 5,000 Daltons to about 20,000 Daltons and an acid number from about 150 to about 250 and wherein the polymeric pigment dispersant is soluble in an alkali solution, and
wherein the polymeric carrier comprises at least a styrene or an acrylic group,
wherein the grafted pigment dispersing polymeric additive is capable of adsorbing to an opacifying pigment, and
wherein the additive comprises particles having an average particle size in the range of about 75 nm to about 200 nm in diameter.
6. The grafted pigment dispersing polymeric additive of claim 5 , wherein the acrylic group comprises a methyl methacrylate or a butyl acrylate.
7. The grafted pigment dispersing polymeric additive of claim 5 , wherein the polymeric carrier comprises single-stage polymers.
8. The grafted pigment dispersing polymeric additive of claim 5 , wherein the polymeric carrier comprises multi-stage polymers.
9. The grafted pigment dispersing polymeric additive of claim 8 , wherein the polymeric carrier comprises core-shell polymers.
10. The grafted pigment dispersing polymeric additive of claim 1 , wherein the polymeric pigment dispersant comprises at least about 1% of the total weight of the grafted pigment dispersing polymeric additive.
11. The grafted pigment dispersing polymeric additive of claim 1 , wherein the polymeric pigment dispersant comprises less than about 50% of the total weight of the grafted pigment dispersing polymeric additive.
12. The grafted pigment dispersing polymeric additive of claim 1 , wherein the weight average molecular weight of the polymeric pigment dispersant ranges from about 5,000 Daltons to about 17,000 Daltons.
13. The grafted pigment dispersing polymeric additive of claim 12 , wherein the weight average molecular weight of the polymeric pigment dispersant ranges from about 8,000 Daltons to about 17,000 Daltons.
14. The grafted pigment dispersing polymeric additive of claim 1 wherein the acid number of the polymeric pigment dispersant ranges from about 200 to about 250.
15. A paint composition comprising at least a latex binder, the grafted pigment dispersing polymeric additive of claim 1 , and an opacifying pigment.
16. The paint composition of claim 15 , wherein the opacifying pigment comprises titanium dioxide.
17. The paint composition of claim 15 , wherein the weight ratio of the latex binder and the grafted pigment dispersing polymeric additive is 1:50 to 50:1.
18. The grafted pigment dispersing polymeric additive of claim 1 , wherein the average particle size is in the range of about 75 nm to 177 nm in diameter.
19. The grafted pigment dispersing polymeric additive of claim 18 , wherein the average particle size is in the range of about 75 nm to 137 nm in diameter.
20. The grafted pigment dispersing polymeric additive of claim 5 , wherein the average particle size is in the range of about 75 nm to 177 nm in diameter.
21. The grafted pigment dispersing polymeric additive of claim 20 , wherein the average particle size is in the range of about 75 nm to 137 nm in diameter.