Surgical suture material with barbs cut into it in the undrawn state
A drawn surgical suture material includes an elongate main body and barbs for anchoring in biological tissues, wherein the barbs are formed by cuts made into the suture material in the undrawn state.
1. A method of producing a surgical suture material comprising:
a) cutting barbs for anchoring in biological tissue into an elongate body of undrawn suture material fiber, and
b) drawing the suture material fiber to form the surgical suture material.
2. The method according to claim 1 , wherein the suture material fiber is twisted before the barbs are cut and is untwisted again after the barbs have been cut.
3. The method according to claim 1 , wherein the barbs are cut with a cutting depth of 5 to 50% mm relative to a diameter of the undrawn suture material fiber.
4. The method according to claim 1 , wherein the barbs are cut at a cutting angle θ of 15 to 50 degrees relative to an outer surface of the undrawn suture material fiber.
5. The method according to claim 1 , wherein the barbs are thermally cut at a temperature of 20 to 100° C. above the melting point of the suture material fiber.
6. The method according to claim 1 , wherein the barbs are cut by a cutting wire.
7. The method according to claim 1 , wherein the barbs are cut by a laser.
8. The method according to claim 1 , wherein the barbs are mechanically cut by at least one cutting blade.
9. The method according to claim 1 , wherein the suture material fiber is drawn with application of heat at a temperature of 20 to 80° C. above the glass transition temperature of the suture material fiber.
10. The method according to claim 1 , wherein the suture material fiber is drawn at a drawing ratio of 2.5 to 8.