Water-based coating composition
According to a water-based composition characterized by containing a colorant, water, a wetting agent, an amine compound, a hydroxyl group-containing organic solvent and a urethane resin having a polycarbonate group, there is provided a water-based coating composition being capable of easily controlling the gloss of a coating film applied on an object to be coated, having good storage stability, and being excellent in wetting properties to an object to be coated and continuous discharge stability without causing nozzle clogging.
1. A water-based coating composition characterized by containing a colorant, water, a wetting agent, an amine compound, a hydroxyl group-containing organic solvent and a urethane resin having a polycarbonate group, wherein
the hydroxyl group-containing organic solvent consists of (A) a solvent having one hydroxyl group in one molecule and (B) a solvent having two or more hydroxyl groups in one molecule, in which a ratio by mass of (A) the solvent having one hydroxyl group in one molecule to (B) the solvent having two or more hydroxyl groups in one molecule is A:B=100:50 to 100:170,
(A) the solvent having one hydroxyl group in one molecule is at least one selected from the group consisting of ethylene glycol monobutyl ether, ethylene glycol isobutyl ether, ethylene glycol tertiary butyl ether, diethylene glycol monobutyl ether, diethylene glycol isobutyl ether, and triethylene glycol monobutyl ether,
(B) the solvent having two or more hydroxyl groups in one molecule is at least one selected from the group consisting of ethylene glycol, diethylene glycol, triethylene glycol, 1,2-propanediol, 2-methyl-1,3-propanediol, 1,2-butanediol, 1,4-butanediol, 3-methyl-1,3-butanediol, glycerin, dipropylene glycol and tripropylene glycol, and
the amine compound is at least one selected from the group consisting of ethanolamine, diethanolamine, triethanolamine, N,N-dimethylethanolamine, N,N-diethylethanolamine, N,N-dibutylethanolamine, N-methyldiethanolamine, N-ethyldiethanolamine, and N-butyldiethanolamine.
2. A water-based coating composition according to claim 1 , wherein the amine compound has a boiling point in a range from a temperature lower by 60° C. than the boiling point of a solvent having the lowest boiling point in the hydroxyl group-containing organic solvent to a temperature higher by 170° C. than the boiling point of the solvent having the lowest boiling point in the hydroxyl group-containing organic solvent.
3. A water-based coating composition according to claim 2 , wherein the amine compound has a boiling point in a range from a temperature lower by 20° C. than the boiling point of a solvent having the lowest boiling point in the hydroxyl group-containing organic solvent to a temperature higher by 170° C. than the boiling point of the solvent having the lowest boiling point in the hydroxyl group-containing organic solvent.
4. A water-based coating composition according to claim 1 , wherein a ratio by mass of (A) a solvent having one hydroxyl group in one molecule to (B) a solvent having two or more hydroxyl groups in one molecule in the hydroxyl group-containing organic solvent is A:B=100:50 to 100:150.
5. A water-based coating composition according to claim 1 , wherein a ratio by mass of the amine compound to the hydroxyl group-containing organic solvent is 0.0005-0.1.
6. A water-based coating composition according to claim 1 , wherein the urethane resin having a polycarbonate group is a urethane dispersion or urethane emulsion having an average particle diameter of 30 nm to 300 nm.
7. A water-based coating composition according to claim 1 , which further comprises an acrylic dispersion or acrylic emulsion having a glass transition temperature Tg of not less than 60° C. and an average particle diameter of 50 nm to 200 nm.
8. A water-based coating composition according to claim 1 , wherein a total amount of an organic solvent in the water-based coating composition is 20% by mass to 55% by mass.
9. A water-based coating composition according to claim 2 , wherein a ratio by mass of the amine compound to the hydroxyl group-containing organic solvent is 0.0005-0.1.
10. A water-based coating composition according to claim 3 , wherein a ratio by mass of the amine compound to the hydroxyl group-containing organic solvent is 0.0005-0.1.
11. A water-based coating composition according to claim 4 , wherein a ratio by mass of the amine compound to the hydroxyl group-containing organic solvent is 0.0005-0.1.
12. A water-based coating composition according to claim 2 , wherein the urethane resin having a polycarbonate group is a urethane dispersion or urethane emulsion having an average particle diameter of 30 nm to 300 nm.
13. A water-based coating composition according to claim 3 , wherein the urethane resin having a polycarbonate group is a urethane dispersion or urethane emulsion having an average particle diameter of 30 nm to 300 nm.
14. A water-based coating composition according to claim 4 , wherein the urethane resin having a polycarbonate group is a urethane dispersion or urethane emulsion having an average particle diameter of 30 nm to 300 nm.
15. A water-based coating composition according to claim 5 , wherein the urethane resin having a polycarbonate group is a urethane dispersion or urethane emulsion having an average particle diameter of 30 nm to 300 nm.