Golf ball having a resilient material
A rebound resilient golf ball having one or more core layers, a cover surrounding the core layer or layers, and optionally a mantle layer positioned between the cover and the core layer or layers. At least one of the layers of the golf ball includes a material whose resilience increases as the hardness of the material increases.
1. A method of manufacturing a golf ball comprising:
forming a core layer, wherein the core layer is made from a first material;
forming a mantle layer, wherein the mantle layer substantially surrounds the core layer, and wherein the mantle layer is made from a second material;
forming a cover layer, wherein the cover layer substantially surrounds the core layer, and wherein the cover layer is made from a third material;
wherein the third material comprises a resilient material,
wherein the resilient material has a resilience value and a hardness value, and wherein the resilient material is thermoplastic polyurethane formed from one or more polyisocyanate monomers and one or more hyper branched polyols having a hydroxy valence of from about 2.1 to about 36, and
wherein the resilient material is formed by curing the mixture to form a product;
wherein the method further comprises grinding the product at a temperature from about 0° C. to about 50° C. to form a ground product; and wherein forming the cover layer comprises extruding or injection molding the ground product.
2. The method of manufacturing a golf ball of claim 1 , wherein the step of forming the core layer comprises compression molding.
3. The method of manufacturing a golf ball of claim 1 , wherein the step of forming the cover layer comprises injection molding or extrusion molding.
4. The method of manufacturing a golf ball of claim 1 , wherein the step of forming the mantle layer comprises injection molding.
5. The method of manufacturing a golf ball of claim 1 , wherein a relationship between the resilience value and the hardness value is expressed by an equation, wherein the equation is y=−0.0207x 2 −1.2839x+54.528, where y represents the resilience value in ASTM D2632 percentage and x represents the hardness value in Shore D units, and wherein the square of the correlation coefficient of the equation is about 0.81.
6. The method of manufacturing a golf ball of claim 1 , wherein the hyper branched polyol has a hydroxy valence of from about 12 to about 36.
7. The method of manufacturing a golf ball of claim 1 , wherein the thermoplastic polyurethane formed from the one or more polyisocyanate monomers and the one or more hyper branched polyols having a hydroxy valence of from about 2.1 to about 36 is further formed from one or more additional polyols.
8. The method of manufacturing a golf ball of claim 1 , wherein the thermoplastic polyurethane formed from the one or more polyisocyanate monomers and the one or more hyper branched polyols having a hydroxy valence of from about 2.1 to about 36 is further formed from one or more chain extenders.
9. The method of manufacturing a golf ball of claim 1 , wherein the thermoplastic polyurethane is formed from, based on a total reaction mixture, from about 15 to about 60 parts by weight of the one or more polyisocyanate monomers, from about 0.1 to about 10 parts by weight of the one or more hyper branched polyols, from about 30 to about 70 parts by weight of optional one or more bio-renewable polyether polyols, and from about 10 to about 40 parts by weight of optional one or more chain extenders.