Printing ink
This invention relates to a printing ink and in particular to an ink for ink-jet printing which is cured by irradiation. The ink comprises at least one radiation-curable monomer; at least one passive thermoplastic resin; at least one radical photoinitiator; and at least one colouring agent; wherein the ink has a viscosity of less than 100 mPas at 25° C., and wherein the at least one passive resin is present at 2 to 15 wt % based on the total weight of the ink and has a molecular weight of 1,500 to 70,000.
1. An ink-jet ink substantially free of water and volatile organic solvents consisting essentially of at least one radiation-curable monomer, wherein the radiation-curable monomer is a monofunctional monomer and the ink contains no more than 15 wt % of multifunctional monomers based on the total weight of the ink; at least one passive thermoplastic resin; 4-10% by weight of at least one radical photoinitiator based on the weight of the ink; and at least one dispersible pigment; wherein the ink has a viscosity of less than 100 mPas at 25° C., wherein the at least one passive resin is present at 2 to 15 wt % based on the total weight of the ink and has a weight-average molecular weight of 1,500 to 70,000.
2. An ink-jet ink as claimed in claim 1 , wherein the radiation-curable monomer is a (meth)acrylate monomer.
3. An ink-jet ink as claimed in claim 1 , wherein the at least one passive resin is present in an amount of from 3 to 10 wt % based on the total weight of the ink.
4. An ink-jet ink as claimed in claim 1 , wherein the at least one passive resin has a weight-average molecular weight of 2,000 to 30,000.
5. An ink-jet ink as claimed in claim 1 wherein the at least one passive resin has a glass transition temperature of 20 to 150° C.
6. An ink-jet ink as claimed in claim 1 , wherein the at least one passive resin has a melting point range falling within the range of 30 to 150° C.
7. An ink-jet ink as claimed in claim 1 , wherein the at least one passive resin is selected from an acrylic resin, an epoxy resin, a ketone resin, a nitrocellulose resin, a phenoxy resin, a polyester resin, a PVC resin or a mixture thereof.
8. An ink-jet ink as claimed in claim 7 , wherein the at least one passive resin is an acrylic resin or a mixture of acrylic resins.
9. An ink-jet ink as claimed in claim 8 , wherein the at least one passive resin is a methyl methacrylate-butyl acrylate copolymer having a weight-average molecular weight of 5000 to 7000.
10. An ink-jet ink as claimed in claim 1 , wherein the ink is substantially free of a multifunctional monomer.
11. An ink-jet ink as claimed in claim 1 , wherein the ink contains no more than 10 wt % of an oligomers based on the total weight of the ink.
12. An ink-jet ink as claimed in claim 11 , wherein the ink is substantially free of an oligomer.
13. An ink-jet ink as claimed in claim 3 , wherein the at least one mono functional (meth)acrylate monomer is selected from phenoxyethyl acrylate (PEA), cyclic TMP formal acrylate (CTFA), isobornyl acrylate (IBOA), tetrahydrofurfuryl (THFA), 2-(2-ethoxyethoxy)ethyl acrylate, octa/decyl acrylate (ODA), tridecyl acrylate (TDA), isodecyl acrylate (IDA), lauryl acrylate and mixtures thereof.
14. A method of ink-jet printing, comprising printing the ink-jet ink as claimed in claim 1 on to a substrate and curing the ink.
15. A method of manufacturing a three-dimensional article comprising printing the ink-jet as claimed in claim 1 on to a planar substrate, curing the ink, heating the substrate to a temperature above the glass transition temperature of the substrate, and vacuum forming the substrate to form the three-dimensional article.
16. A substrate having the ink-jet ink as claimed in claim 1 printed thereon.
17. An ink-jet ink consisting essentially of at least one radiation-curable monomer, wherein the radiation-curable monomer is a monofunctional monomer and the ink contains no more than 15 wt % of multifunctional monomers based on the total weight of the ink; at least one passive thermoplastic resin; 4-10% by weight of at least one radical photoinitiator based on the weight of the ink; and at least one dispersible pigment; wherein the ink has a viscosity of less than 100 mPas at 25 ° C., wherein said ink-jet ink is substantially free of water and volatile organic solvents, wherein the at least one passive resin is present at 2 to 15 wt % based on the total weight of the ink and has a weight-average molecular weight of 2,000 to 30,000, and wherein said ink-jet ink is suitable for vacuum forming applications.
18. A method of manufacturing a three-dimensional article comprising printing an ink-jet ink on to a planar substrate, curing the ink, heating the substrate to a temperature above the glass transition temperature of the substrate, and vacuum forming the substrate to form the three-dimensional article, said ink-jet ink consisting essentially of at least one radiation-curable monomer, wherein the radiation-curable monomer is a monofunctional monomer and the ink contains no more than 15 wt % of multifunctional monomers based on the total weight of the ink; at least one passive thermoplastic resin; 4-10% by weight of at least one radical photoinitiator based on the weight of the ink; and at least one dispersible pigment; wherein the ink has a viscosity of less than 100 mPas at 25 ° C., wherein said ink-jet ink is substantially free of water and volatile organic solvents, wherein the at least one passive resin is present at 2 to 15 wt % based on the total weight of the ink and has a weight-average molecular weight of 1,500 to 70,000, and wherein said ink-jet ink is suitable for vacuum forming applications.