Molded article containing stacked carbon fiber and method for producing same

1. A carbon fiber-containing stacked molded article, comprising:

a substrate composed of first carbon fibers piled; and

a woven fabric layer located on at least one surface of the substrate, and formed by weaving carbon fiber spun yarns including second carbon fibers having an average fiber diameter of 12 μm or less, and third carbon fibers having an average fiber diameter in excess of 12 μm, wherein the carbon fiber spun yarns are selected from spun yarns of a core-sheath structure having the second carbon fibers as a core material and the third carbon fibers as a sheath material; doubled and twisted spun yarns composed of spun yarns of a core-sheath structure having the second carbon fibers as a core material and the third carbon fibers as a sheath material; and combinations thereof wherein the second carbon fibers are anisotropic carbon fibers and the third carbon fibers are isotropic carbon fibers.

2. The carbon fiber-containing stacked molded article according to claim 1 , wherein the substrate is a stacked body formed by impregnating a stack of felts, which comprise the first carbon fibers, with a thermosetting resin, or is a carbon fiber stacked body formed by impregnating a stack of felts, which comprise the first carbon fibers, with a thermosetting resin, and then heat-treating the impregnated stacked body of felts.

3. The carbon fiber-containing stacked molded article according to claim 1 , wherein tensile strength of a spun yarn woven fabric constituting the woven fabric layer is 0.2 kN or higher.

4. The carbon fiber-containing stacked molded article according to claim 1 , which has flexural strength of 1.5 MPa or higher, but lower than 5.0 MPa.

5. A heat insulating material comprising the carbon fiber-containing stacked molded article according to claim 1 .

6. The carbon-fiber-containing stacked molded article according to claim 1 , wherein the proportions of the second carbon fibers and the third carbon fibers are blended such that the amount of the second carbon fibers is 10% by mass or more and 90% by mass or less.

7. A carbon fiber-containing stacked molded article, comprising:

a stacked body formed by impregnating a stack of felts, which comprise first carbon fibers, with a thermosetting resin, or a carbon fiber stacked body formed by impregnating a stack of felts, which comprise the first carbon fibers, with a thermosetting resin, and then heat-treating the impregnated stack of felts; and

a woven fabric layer located on at least one surface of the carbon fiber stacked body, and formed by weaving spun yarns selected from spun yarns of a core-sheath structure having second carbon fibers having an average fiber diameter of 12 μm or less as a core material, and third carbon fibers having an average fiber diameter in excess of 12 μm as a sheath material; doubled and twisted spun yarns composed of spun yarns of a core-sheath structure having the second carbon fibers as a core material and the third carbon fibers as a sheath material; and combinations thereof.

8. The carbon fiber-containing stacked molded article according to claim 7 , wherein the second carbon fibers are anisotropic carbon fibers, and the third carbon fibers are isotropic carbon fibers.

9. The carbon fiber-containing stacked molded article according to claim 7 , wherein tensile strength of a spun yarn woven fabric constituting the woven fabric layer is 0.2 kN or higher.

10. The carbon fiber-containing stacked molded article according to claim 7 , which has flexural strength of 1.5 MPa or higher, but lower than 5.0 MPa.

11. A heat insulating material comprising the carbon fiber-containing stacked molded article according to claim 7 .

12. The carbon fiber-containing stacked molded article according to claim 7 , wherein the proportions of the second carbon fibers and the third carbon fibers are blended such that the amount of the second carbon fibers is 10% by mass or more and 90% by mass or less.

13. A method for producing a carbon fiber-containing stacked molded article, comprising:

a substrate preparation step of piling first carbon fibers to prepare a substrate;

a woven fabric formation step of spinning second carbon fibers having an average fiber diameter of 12 μm or less, and third carbon fibers having an average fiber diameter in excess of 12 μm to prepare a carbon fiber spun yarn, and forming a woven fabric from the resulting carbon fiber spun yarn, wherein the carbon fiber spun yarns are selected from spun yarns of a core-sheath structure having the second carbon fibers as a core material and the third carbon fibers as a sheath material; doubled and twisted spun gars composed of spun yarns of a core-sheath structure having the second carbon fibers as a core material and the third carbon fibers as a sheath material; and combinations thereof;

an adhesion step of stacking at least the woven fabric to at least one surface of the substrate by use of an adhesive to form a carbon fiber-containing stacked body having the substrate and a woven fabric layer; and

a heat-treating step of compression molding the carbon fiber-containing stacked body, and then heat-treating the compression molded carbon fiber-containing stacked body.

14. The method according to claim 13 , wherein the substrate preparation step comprises impregnating a stack of felts composed of the first carbon fibers with a thermosetting resin to form a stacked body.

15. The method according to claim 13 , wherein the substrate preparation step comprises impregnating a stack of felts composed of the first carbon fibers with a thermosetting resin, and then heat-treating the impregnated stacked body of felts.

16. The method according to claim 13 , wherein the second carbon fibers are anisotropic carbon fibers, and the third carbon fibers are isotropic carbon fibers.

17. The method according to claim 13 , wherein the proportions of the second carbon fibers and the third carbon fibers are blended such that the amount of the second carbon fibers is 10% by mass or more and 90% by mass or less.