Reduced beryllium casting alloy
The beryllium content of beryllium aluminum alloys suitable for investment casting which contain a small but suitable amount of silver can be significantly reduced without adversely affecting their thermal or investment casting properties by including significantly more silicon in the alloy than done in the past.
1. A beryllium aluminum alloy suitable for investment casting purposes, the alloy comprising 40 to 55 wt. % Be, 3.0-11 wt. % Si, 1.2 to 5.0 wt. % Ag, and no more than 3 wt. % optional ingredients, with the balance being aluminum plus incidental impurities, wherein the Be/Al ratio of the alloy is ≦1.8, the Si/Al ratio of the alloy is ≧0.07, and the combined amounts of Si and Ag in the alloy is ≧5.0 wt. %, and further wherein the alloy has a coefficient of thermal expansion of ≦14.5 μm/m (ppm) and a thermal conductivity of at least 150 W/M-° K@30° C.
2. The alloy of claim 1 , wherein the Be/Al ratio is ≦1.4.
3. The alloy of claim 2 , wherein the Be/Al ratio is ≦1.2.
4. The alloy of claim 1 , wherein the Si/Al ratio is ≧0.085.
5. The alloy of clam 4, wherein the Si/Al ratio is ≧0.1.
6. The alloy of claim 1 , wherein the combined amounts of Si and Ag is ≧6.0 wt. %.
7. The alloy of claim 1 , wherein the thermal conductivity of the alloy is at least 165 W/M-° K@30° C.
8. The alloy of claim 7 , wherein the thermal conductivity of the alloy is at least 180 W/M-° K@30° C.
9. The alloy of claim 1 , wherein the alloy contains 45 to 55 wt. % Be, 3.5-6.0 wt. % Si, 1.4 to 4.0 wt. % Ag, and no more than 1.5 wt. % optional ingredients, with the balance being aluminum plus incidental impurities, wherein the Be/Al ratio is ≦1.4, the Si/Al ratio is ≧0.085, and the alloy has a thermal conductivity of at least 165 W/M-° K@30° C.
10. The alloy of claim 9 , wherein the alloy contains 47.5 to ≦50 wt. % Be, 4.0-5.0 wt. % Si, 1.65-2.35 wt. % Ag, and no more than 0.5 wt. % optional ingredients, with the balance being aluminum plus incidental impurities, and wherein the Be/Al ratio is ≦1.4, the Si/Al ratio is ≧0.085, and the alloy has a thermal conductivity of at least 180 W/M-° K@30° C.
11. The alloy of claim 9 , wherein the alloy contains 0.01 to 0.1 wt. % strontium, sodium, calcium, antimony or mixtures thereof.
12. The alloy of claim 11 , wherein the alloy contains 0.02 to 0.06 wt. % strontium.
13. The alloy of an claim 1 , wherein the alloy is essentially free of Co, Ni and Cu.