Fluorographene and preparation method thereof
View Patent ↗A fluorographene and preparation method thereof are provided. For the said fluorographene, the fraction of F is 0.5<F %<53.5% in weight and the fraction of C is 46.5%<C %<99.5% in weight. The method comprises the following steps: providing the graphite; preparing the graphene oxide with the graphite; mixing the graphene oxide with the compound containing fluorine by weight ratio of 1:1˜100:1 in anaerobic environment, reacting at 200˜1 000° C. for 1˜10 hours then cooling down to obtain the said fluorographene. The above-mentioned method using graphite to prepare the graphene oxide, then making use of the reaction of graphene oxide with the compound containing fluorine under a certain temperature has simple process and can prepare fluorographene conveniently.
1. A preparation method of fluorographene, wherein the mass fraction of F is in the range of 0.5%<F%<53.5% and the mass fraction of C is in the range of 46.5%<C% <99.5%, comprising: providing graphite; preparing graphene oxide with said graphite; mixing said graphene oxide with a compound containing a fluorine by mass ratio of 1:1˜100:1 in an oxygen-free environment, then reacting at 200˜1000° C. for 1˜10 hours, then cooling down to obtain said fluorographene.
2. The preparation method of fluorographene as claimed in claim 1 , wherein, said compound containing fluorine is at least one of ammonium fluoride, sodium fluoroborate, potassium fluoroborate, potassium fluoroaluminate and sodium fluorosilicate.
3. The preparation method of fluorographene as claimed in claim 1 , wherein, said compound containing fluorine at least one of polytetrafluoroethylene, polyhexafluoropropylene and polyvinylidene fluoride.
4. The preparation method of fluorographene as claimed in claim 1 , wherein the mass ratio of said graphene oxide to said compound containing fluorine is in the range of 1:1˜1:50.
5. The preparation method of fluorographene as claimed in claim 1 , wherein said graphene oxide reacts with said compound containing fluorine at 500˜800° C. to obtain said fluorographene.
6. The preparation method of fluorographene as claimed in claim 1 , wherein, further comprising purification process that: after obtaining said fluorographene, washing said fluorographene successively with water and ethanol, then drying.
7. The preparation method of fluorographene as claimed in claim 1 , wherein, degree of purity of said graphite is higher than 99.5%.
8. The preparation method of fluorographene as claimed in claim 2 , wherein the mass ratio of said graphene oxide to said compound containing fluorine is in the range of 1:1˜1:50.
9. The preparation method of fluorographene as claimed in claim 3 , wherein the mass ratio of said graphene oxide to said compound containing fluorine is in the range of 1:1˜1:50.
10. The preparation method of fluorographene as claimed in claim 2 , wherein said graphene oxide reacts with said compound containing fluorine at 500˜800° C. to obtain said fluorographene.
11. The preparation method of fluorographene as claimed in claim 3 , wherein said graphene oxide reacts with said compound containing fluorine at 500˜800° C. to obtain said fluorographene.