Alumina nanotube/nanorod supported hydrodesulfurization nanocatalyst, method of preparation and application
The invention relates to a hydrodesulfurization nanocatalyst, use of the hydrodesulfurization nanocatalyst in a hydrodesulfurization process and a process for producing the hydrodesulfurization nanocatalyst. The hydrodesulfurization nanocatalyst can include a nanostructured alumina material, at least one metal selected from group VI B of the periodic table of elements, and at least one metal selected from group VIII B of the periodic table of elements.
1. A hydrodesulfurization nanocatalyst comprising: a nanostructured alumina material; at least one metal selected from group VI B of the periodic table of elements, and at least one metal selected from group VIII B of the periodic table of elements, wherein the molar ratio of the metal selected from group VI B of the periodic table of elements to the metal selected from group VIII B of the periodic table of elements is from about 0.2 to about 0.5 and wherein the metals are present on the nanostructured alumina material in a form of multilayer nanoclusters wherein the catalyst further comprises zeolite HY and B 2 O 3 in a ratio of about 1:0.5.
2. The hydrodesulfurization nanocatalyst according to claim 1 , wherein the nanostructured alumina material comprises at least one of alumina nanorods and alumina nanotubes.
3. The hydrodesulfurization nanocatalyst according to claim 1 , wherein the nanostructured alumina material is nanostructured gamma-alumina.
4. The hydrodesulfurization nanocatalyst according to claim 1 , wherein the nanostructured alumina material includes a surface area of from about 450 to about 800 m 2 /g.
5. The hydrodesulfurization nanocatalyst according to claim 1 , wherein the nanostructured alumina material includes a pore volume of from about 0.8 to about 3 cm 3 /g.
6. The hydrodesulfurization nanocatalyst according to claim 1 , wherein the nanostructured alumina material includes a mesoporous pore diameter of from about 9 to about 30 nm.
7. The hydrodesulfurization nanocatalyst according to claim 1 , wherein the at least one metal selected from group VIB of the periodic table of elements and the at least one metal selected from group VIIIB of the periodic table of elements are present in an amount of from about 1 to about 30% by weight.
8. The hydrodesulfurization nanocatalyst according to claim 1 , wherein the at least one metal selected from group VIB of the periodic table of elements comprises at least one of molybdenum and tungsten.
9. The hydrodesulfurization nanocatalyst according to claim 1 , wherein the at least one metal selected from group VIIIB of the periodic table of elements comprises at least one of nickel and cobalt.
10. The hydrodesulfurization nanocatalyst according to claim 1 , further comprising P 2 O 5 .
11. A method for removing sulfur from a stream comprising the step of contacting the stream with the hydrodesulfurization nanocatalyst of claim 1 .
12. A process for producing a hydrodesulfurization nanocatalyst according to claim 1 comprising the steps of: providing a solution of at least one metal; impregnating the nanostructured alumina material in a solution comprising at least one metal to create a catalyst; and drying the catalyst.