Aqueous polyurethane-polyurea dispersions
The present invention relates to aqueous polyurethane-polyurea dispersions which stabilize a foam—produced by mechanical expansion—without addition of further foam-stabilizing components in such a way that aqueous foams are obtainable which are stable both during temporary storage and during processing, so that they can be applied in the form of foam also by customary application methods and substantially retain the foam structure even after drying.
1. Process for the preparation of a foam-stabilising aqueous polyurethane-polyurea dispersion, comprising the steps of
A) first a polyurethane prepolymer containing NCO groups—having an NCO functionality of less than two—is produced by reacting
A1) polyisocyanates with
A2) polymeric polyols, polyamines, or a mixture thereof, wherein the polymeric polyols, polyamines, or mixture thereof have number average molecular weights of 400 to 8000 g/mol,
A3) isocyanate-reactive, non-ionically hydrophilising compounds which are polyoxyalkylene ethers which contain at least one hydroxyl or amino group,
A4) isocyanate-reactive compounds containing C 7-24 -alkyl or C 7-24 -alkenyl groups, and having 2, 3, or 4 isocyanate-reactive groups, and
A6) isocyanate-reactive, ionically or potentially ionically hydrophilising compounds,
and
B) the still free NCO groups of the prepolymer are reacted with a compound A8), wherein the compound A8) is selected from the group consisting of isocyanate-reactive amino alcohols, monoamines, polyamines, hydrazine, hydrazides and mixtures thereof, in an amount such that a theoretical ratio of the isocyanate-reactive NH groups of the compound A8) to the NCO groups of the prepolymer from 0.8 to 1.2 is achieved,
wherein no foam-stabilizing additives are included in said dispersion.
2. Process according to claim 1 , wherein the polyurethane prepolymer containing NCO groups has a NCO functionality of more than one and less than two.
3. Process according to claim 1 wherein, in step A), a reaction of A1) with
A5) low molecular weight compounds having number average molecular weights of 17-400 g/mol, selected from the group consisting of mono- and polyalcohols, mono- and polyamines and amino alcohols, and/or wherein
A7) in step A), the reaction of A1) with A2) to A4 and/or A5) and/or A6) takes place in aliphatic ketones or esters as solvents.
4. Process according to claim 3 , wherein
C) either the prepolymer obtained from step A) is dissolved in aliphatic ketones or esters or, if the preparation was carried out in the presence of A7), the prepolymer solution is diluted by further addition of aliphatic ketones or esters.
5. Process for the preparation of aqueous polyurethane-polyurea dispersions according to claim 1 wherein the polyurethane prepolymer containing NCO groups contains 10 to 45% by weight units of component A1), 30 to 80% by weight units of component A2), 0.1 to 15% by weight units of component A3) and 0.1 to 15% by weight units of component A4), the sum of all components units being 100% by weight.
6. Process according to claim 1 , wherein the compounds according to A4) contain at least one straight, saturated alkyl chain of 11 to 22 carbon atoms.
7. Process according to claim 6 , wherein the compounds according to A4) contain at least one straight, saturated alkyl chain of 15 to 20 carbon atoms.
8. Process according to claim 1 , wherein the compounds according to A3) are polyethylene glycol propylene glycol monoalkyl ethers, mixtures of polyethylene glycol monoalkyl ethers and polypropylene glycol monoalkyl ethers or mixtures thereof.
9. Process according to claim 1 , wherein the polyisocyanates A1) have the formula X(NCO) p , in which p is 2, and X is an aliphatic or cycloaliphatic, aromatic or araliphatic hydrocarbon radical.
10. An aqueous foam-stabilising polyurethane-polyurea dispersion made by a process comprising the steps of
A) first a polyurethane prepolymer containing NCO groups—having an NCO functionality of less than two—is produced by reacting
A1) polyisocyanates with
A2) polymeric polyols, polyamines, or a mixture thereof, wherein the polymeric polyols, polyamines, or mixture thereof have number average molecular weights of 400 to 8000 g/mol,
A3) isocyanate-reactive, non-ionically hydrophilising compounds which are polyoxyalkylene ethers which contain at least one hydroxyl or amino group,
A4) isocyanate-reactive compounds containing C 7-24 -alkyl or C 7-24 -alkenyl groups and having 2, 3, or 4 isocyanate-reactive groups, and
A6) isocyanate-reactive, ionically or potentially ionically hydrophilising compounds
and
B) the still free NCO groups of the prepolymer are reacted with a compound A8), wherein the compound A8) is selected from the group consisting of isocyanate-reactive amino alcohols, monoamines, polyamines, hydrazine, hydrazides and mixtures thereof, in an amount such that a theoretical ratio of the isocyanate-reactive NH groups of the compound A8) to the NCO groups of the prepolymer from 0.8 to 1.2 is achieved,
wherein no foam-stabilizing additives are included in said dispersion.
11. A coating made from an aqueous polyurethane-polyurea dispersion according to claim 10 .
12. A coating produced from foam, wherein the foam is produced by mechanical expansion and wherein the foam comprises an aqueous polyurethane-polyurea dispersion according to claim 10 .
13. The coating according to claim 11 , wherein the aqueous polyurethane-polyurea dispersion is in the form of a foam and wherein the foam is created by mechanical expansion.
14. A substrate coated with a coating according to claim 11 .
15. Leather or imitation leather coated with a coating according to claim 11 .
16. Full-grain leather, buffed leather or split leather coated with a coating according to claim 11 .
17. A substrate coated with a coating according to claim 13 .
18. Leather or imitation leather coated with a coating according to claim 13 .
19. Full-grain leather, buffed leather or split leather coated with a coating according to claim 13 .