Porous magnetic sorbent
The invention relates to the field of producing polymer sorbents having magnetic properties, and can be used for removing petroleum products from a water surface. A magnetic porous sorbent for removing thin petroleum films from a water surface is proposed, said sorbent being produced on the basis of industrial synthetic divinyl rubber, as a result of the modification thereof by an oxidative chlorophosphorylation reaction with subsequent immobilization of magnetite FeO nanoparticles; and a method for producing a magnetic material is proposed, said method comprising the formation of FeO nanoparticles by an ion deposition method directly within a porous polymer matrix. The sorbent has a good sorption capacity in relation to thin petroleum films.
1. A porous magnetic sorbent, comprising
a polymer porous matrix comprising a synthetic divinyl rubber functionalized by phosphone and phosphate groups; and
a magnetic material attached to the polymer porous matrix, comprising nano-particles of Fe 3 O 4 .
2. The sorbent of claim 1 , wherein the functionalized synthetic divinyl rubber is prepared using oxidizing chlorophosphorylation.
3. The sorbent of claim 1 , wherein the sorbent sorbes at least about 0.2 gram of oil per 1 gram of sorbent.
4. A method for preparing a porous magnetic solvent comprising:
modifying a synthetic divinyl rubber using oxidizing chlorophosphorylation to produce a modified synthetic rubber with phosphon- and phosphatedichlorinade-groups;
hydrolyzing the modified synthetic divinyl rubber with phosphon- and phosphatedichlorinade-groups to produce a modified synthetic divinyl rubber with phosphone and phosphate groups; and
sorption of nano-sized particles Fe 3 O 4 into the modified synthetic divinyl rubber with phosphone and phosphate groups.
5. The method of claim 4 , wherein the oxidizing chlorophosphorylation is carried out using PCl 3 in the presence of O 2 in CCl 4 .
6. The method of claim 4 , wherein the sorption occurs through ionic layering.
7. The method of claim 4 , wherein the nano-sized particles of Fe 3 O 4 are received in the modified synthetic divinyl rubber with phosphone and phosphate groups by chemical coprecipitation of the iron salts FeCl 2 and FeCl 3 in an alkaline environment.
8. The method of claim 4 , further comprising foaming HCl formed during the oxidizing chlorophosphorylation of synthetic divinyl rubber step.