Method for producing conductive material, conductive material obtained by the method, electronic device containing the conductive material, and light-emitting device

1. method for producing a conductive material, comprising the step of heating a conductive material composition, the conductive material composition consisting essentially of:

at least one of a full-cured or semi-cured thermosetting resin in a particulate form and a thermoplastic resin in a particulate form;

particles made of silver;

a metal oxide which is one or more selected from the group consisting of AgO, Ag 2 O, and Ag 2 O 3 ; and

an organic solvent having a boiling point of 300° C. or lower, or water.

2. The method for producing a conductive material according to claim 1 , wherein the thermosetting resin or the thermoplastic resin is in a particulate form having an average particle diameter of 0.1 μm to 10 μm both inclusive.

3. The method for producing a conductive material according to claim 1 , wherein an added amount of the full-cured thermosetting resin is more than 0 wt % and not more than 5 wt % with respect to a weight of the silver particles.

4. The method for producing a conductive material according to claim 1 , wherein an added amount of the semi-cured thermosetting resin is more than 0 wt % and not more than 10 wt % with respect to a weight of the silver particles.

5. The method for producing a conductive material according to claim 1 , wherein an added amount of the thermoplastic resin is more than 0 wt % and not more than 10 wt % with respect to a weight of the silver particles.

6. The method for producing a conductive material according to claim 1 , wherein the full-cured thermosetting resin has a glass transition temperature (Tg) of either −40° C. or lower, or 100° C. or higher.

7. The method for producing a conductive material according to claim 1 , wherein the semi-cured thermosetting resin has a glass transition temperature (Tg) of 100° C. or higher.

8. The method for producing a conductive material according to claim 1 , wherein the thermoplastic resin has a glass transition temperature (Tg) or a melting point of 100° C. or higher.

9. The method for producing a conductive material according to claim 1 , wherein the organic solvent contains at least any of a lower alcohol, and a lower alcohol having one or more substituents selected from the group consisting of: methoxy, ethoxy, n-propoxy, i-propoxy, n-butoxy, i-butoxy, sec-butoxy, t-butoxy, or n-pentyloxy; methoxy, ethoxy, n-propoxy, i-propoxy, n-butoxy, i-butoxy, sec-butoxy, t-butoxy, or n-pentyloxy substituted with methoxy, ethoxy, n-propoxy, i-propoxy, n-butoxy, i-butoxy, sec-butoxy, t-butoxy, or n-pentyloxy; amino; and halogen.

10. The method for producing a conductive material according to claim 1 , wherein a temperature for heating in the heating step is in a range of 150° C. to 400° C.

11. The method for producing a conductive material according to claim 1 , wherein, in the case where the silver particles are of one type having one average particle diameter (median diameter), the average particle diameter (median diameter) is 0.1 μm to 15 μm.

12. The method for producing a conductive material according to claim 1 , wherein, in the case where the silver particles are a mixture of two types having respective average particle diameters (median diameters) in combination, the combination is one type having an average particle diameter (median diameter) in a range of 0.1 μm to 15 μm and the other type having an average particle diameter (median diameter) in a range of 0.1 μm to 15 μm.

13. A method for producing a conductive material, comprising the step of heating a conductive material composition, which does not include a metal oxide, in an atmosphere of oxygen, ozone, or air, the conductive material composition consisting essentially of:

at least one of a full-cured or semi-cured thermosetting resin in a particulate form and a thermoplastic resin in a particulate form;

particles made of silver; and

an organic solvent having a boiling point of 300° C. or lower, or water,

wherein, in the case where the particles made of silver are of one type having one average particle diameter (median diameter), the average particle diameter median diameter is 0.1 μm to 15μm.

14. The method for producing a conductive material according to claim 13 , wherein the thermosetting resin or the thermoplastic resin is in a particulate form having an average particle diameter of 0.1 μm to 10 μm both inclusive.

15. The method for producing a conductive material according to claim 13 , wherein an added amount of the thermoplastic resin is more than 0 wt % and not more than 10 wt % with respect to a weight of the silver particles.

16. The method for producing a conductive material according to claim 13 , wherein the thermoplastic resin has a glass transition temperature (Tg) or a melting point of 100° C. or higher.

17. The method for producing a conductive material according to claim 13 , wherein the organic solvent contains at least any of a lower alcohol, and a lower alcohol having one or more substituents selected from the group consisting of: methoxy, ethoxy, n-propoxy, i-propoxy, n-butoxy, i-butoxy, sec-butoxy, t-butoxy, or n-pentyloxy; methoxy, ethoxy, n-propoxy, i-propoxy, n-butoxy, i-butoxy, sec-butoxy, t-butoxy, or n-pentyloxy substituted with methoxy, ethoxy, n-propoxy, i-propoxy, n-butoxy, i-butoxy, sec-butoxy, t-butoxy, or n-pentyloxy; amino; and halogen.

18. The method for producing a conductive material according to claim 13 , wherein a temperature for heating in the heating step is in a range of 150° C. to 400° C.