Chromium-free silicate-based ceramic compositions
A composition based on a certain chromium-free silicate-based binder is described. The one-part slurry composition is an aqueous solution of lithium-doped potassium silicate in combination with an aluminum or aluminum alloy powder. The one-part slurry composition produces a corresponding coating exhibiting improved performance at a reduced coating thickness.
1. An aqueous slurry composition for the production of a coating on a substrate comprising:
a binder comprising an aqueous solution of lithium doped potassium silicate, the binder characterized by an absence of chromium; and
an aluminum or aluminum alloy powder incorporated into the binder, wherein the aluminum or the aluminum alloy powder and the binder are contained as a one-part composition;
wherein the aluminum or aluminum alloy powder comprises a particle size distribution characterized in that the 50 th percentile of the particle size distribution has a diameter of between about 4 to 7 microns and the 90 th percentile of the particle size distribution has a diameter of less than or equal to about 11.5-15.5 microns.
2. The aqueous slurry composition of claim 1 , wherein the lithium doped potassium silicate and aluminum or aluminum alloy powder are contained in a weight ratio of about 0.18:1 to 0.46:1 silicate to aluminum or aluminum alloy powder.
3. The aqueous slurry composition of claim 1 , wherein the aluminum or aluminum alloy powder in the slurry is between about 35-45 weight percent (wt %) based on the total weight of the slurry and the silicate to aluminum is contained in a ratio of about 0.22:1 to 0.37:1 by weight.
4. The aqueous slurry composition of claim 1 , further comprising chromium-free corrosion inhibitors.
5. The aqueous slurry composition of claim 1 ,
further comprising the aluminum alloy powder selected from the group consisting of aluminum-silicon, aluminum-copper and aluminum-magnesium.
6. An article of manufacture comprising a substrate with a coating formed from a slurry with a composition according to claim 1 .
7. An aqueous slurry composition for the production of a coating on a substrate comprising:
a binder comprising an aqueous solution of lithium doped potassium silicate, the binder characterized by an absence of chromium; and
an aluminum or aluminum alloy powder incorporated into the binder, wherein the aluminum or the aluminum alloy powder and the binder are contained as a one-part composition;
wherein the aluminum or aluminum alloy powder content in the slurry is between about 30-50 weight percent (wt %) based on the total weight of the slurry and further comprises a particle size distribution characterized in that the 50 th percentile of the particle size distribution has a diameter of between about 3.9 to 4.5 microns and the 90 th percentile of the particle size distribution has a diameter of less than or equal to about 9.0 microns.
8. An aqueous slurry composition for the production of a coating on a substrate, comprising:
a binder comprising an aqueous solution of lithium doped potassium silicate, the binder characterized by an absence of chromium; and
an aluminum or aluminum alloy powder incorporated into the binder, wherein the aluminum or the aluminum alloy powder and the binder are contained as a one-part composition;
wherein the lithium-doped potassium silicate comprises potassium and lithium in a ratio of about 3:1 to 20:1 by weight as K 2 O:Li 2 O, and further wherein the ratio of silicate to potassium is in a ratio of about 2:1 to 3:1 by weight as SiO 2 :K 2 O.
9. The aqueous slurry composition of claim 8 , wherein the lithium-doped potassium silicate comprises potassium and lithium in the ratio of about 7:1 to 11:1 by weight as K 2 O:Li 2 O, and further wherein the ratio of silicate to potassium is of about 2.4:1 to 2.8:1 by weight as SiO 2 :K 2 O.
10. A coating composition for a substrate comprising:
a ceramic matrix not containing chromium, said matrix formed by a silicate binder and a plurality of aluminum powder particles embedded within said matrix;
wherein said silicate binder is potassium silicate doped with lithium;
of
wherein the aluminum powder comprises a particle size distribution characterized in that the 50 th percentile of the particle size distribution has a diameter of between about 4 to 7 microns and the 90 th percentile of the particle size distribution has a diameter of less than or equal to about 11.5-15.5 microns.
11. The coating composition of claim 10 , wherein the silicate and aluminum are contained in a weight ratio of about 0.18:1 to 0.46:1 silicate to aluminum.
12. The coating composition of claim 10 , wherein the coating is capable of being modified to a conductive coating with sacrificial corrosion protection.
13. The coating composition of claim 10 produced from an aqueous slurry, wherein the aluminum powder is contained in the slurry in an amount between about 30-50 weight percent (wt %) based on the total weight of the slurry.
14. The coating composition of claim 10 , produced from an aqueous slurry, wherein the aluminum powder in the slurry is between about 35-45 weight percent (wt %) based on the total weight of the slurry, and the lithium doped potassium silicate to aluminum weight ratio is about 0.22:1 to 0.37:1.
15. A coating composition for a substrate comprising:
a ceramic matrix not containing chromium, said matrix formed by a silicate binder and a plurality of aluminum powder particles embedded within said matrix;
wherein said silicate binder is potassium silicate doped with lithium
wherein the aluminum powder comprises a particle size distribution characterized in that the 50 th percentile of the particle size distribution has a diameter of between about 3.9 to 4.5 microns and the 90 th percentile of the particle size distribution has a diameter of less than or equal to about 9.0 microns.