Method of manufacturing electrodes using carbon nanotube sheets
Growing spin-capable multi-walled carbon nanotube (MWCNT) forests in a repeatable fashion will become possible through understanding the critical factors affecting the forest growth. Here we show that the spinning capability depends on the alignment of adjacent MWCNTs in the forest which in turn results from the synergistic combination of a high areal density of MWCNTs and short distance between the MWCNTs. This can be realized by starting with both the proper Fe nanoparticle size and density which strongly depend on the sheet resistance of the catalyst film. Simple measurement of the sheet resistance can allow one to reliably predict the growth of spin-capable forests. The properties of pulled MWCNTs sheets reflect that there is a relationship between their electrical resistance and optical transmittance. Overlaying either 3, 5, or 10 sheets pulled out from a single forest produces much more repeatable characteristics.
1. A method of manufacturing an electrode for fuel cells and lithium batteries comprising the step of:
(i) pulling out a bundle of CNTs from a CNT forest;
(ii) forming CNT sheets from the pulled bundle of the CNTs; and
(iii) forming metal oxide/CNT sheet composites comprising CNT sheets, wherein the CNTs are encapsulated by the metal oxide.
2. The method of claim 1 , wherein the metal oxide comprises a transition metal oxide.
3. The method of claim 2 , wherein the transition metal oxide is selected from the group consisting of manganese oxide, nickel oxide, cobalt oxide, and iron oxide.
4. The method of claim 1 , wherein the metal oxide is coated onto the CNTs by a process selected from the group consisting of sputtering, electro-deposition, chemical vapor deposition (CVD), and combinations thereof.
5. The method of claim 1 , wherein
(i) the CNTs are encapsulated by the metal oxide by a process comprising coating a metal onto the CNTs, wherein the process is selected from the group consisting of sputtering, electro-deposition, CVD, and combinations thereof; and,
(ii) oxidizing the metal using oxidants.
6. The method of claim 5 , wherein the oxidants are selected from the group consisting of oxygen, ozone, hydrogen peroxide, and nitric acid.
7. The method of claim 1 , wherein the method is a method of manufacturing at least two electrodes for a fuel cell or a lithium battery.
8. A method of manufacturing an electrode:
(i) pulling out a bundle of CNTs from a CNT forest;
(ii) forming CNT sheets from the pulled bundle of the CNTs; and
(iii) forming metal oxide/CNT sheet composites comprising the CNT sheets, wherein the CNTs are encapsulated by the metal oxide, wherein the electrode is for a device selected from the group consisting of solar cells, LEDs, fuel cells, and lithium batteries.
9. The method of claim 8 , wherein the metal oxide comprises a transition metal oxide.
10. The method of claim 9 , wherein the transition metal oxide is selected from the group consisting of manganese oxide, nickel oxide, cobalt oxide, and iron oxide.
11. The method of claim 8 , wherein the metal oxide is coated onto the CNTs by a process selected from the group consisting of sputtering, electro-deposition, chemical vapor deposition (CVD), and combinations thereof.
12. The method of claim 8 , wherein
(i) the CNTs are encapsulated by the metal oxide by a process comprising coating a metal onto the CNTs, wherein the process is selected from the group consisting of sputtering, electro-deposition, CVD, and combinations thereof; and,
(ii) oxidizing the metal using oxidants.
13. The method of claim 12 , wherein the oxidants are selected from the group consisting of oxygen, ozone, hydrogen peroxide, and nitric acid.
14. The method of claim 8 , wherein the method is a method of manufacturing at least two electrodes for a solar cell, a LED, a fuel cell, or a lithium battery.